Crystallization and characteristics of {100}-oriented diamond with CH4N2S additive under high pressure and high temperature

doi:10.1088/1674-1056/ab99b9

Abstract Diamond crystallization was carried out with CH₄N₂S additive in the FeNiCo-C system at pressure 6.0 GPa and temperature ranging from 1290 ℃ to 1300 ℃. The crystallization qualities of the synthetic crystals were characterized by Raman spectra and the Raman peaks located at 1331 cm^-1. Fourier transform infrared (FTIR) results showed that the hydrogen-related absorption peak of the as-grown diamond was at 2920 cm^-1, respectively. Interestingly, A-center nitrogen was observed in the obtained diamond and the characteristic absorption peaks located at 1095 cm^-1 and 1282 cm^-1. Especially, the absorption peak at 1426 cm^-1 attributing to the aggregation B-center nitrogen defect was distinctly found when the CH₄N₂S content reached 0.3 mg in the synthesis system, which was extremely rare in synthetic diamond. Furthermore, optical color centers in the synthesized crystals were investigated by photoluminescence (PL).

Keywords: high pressure and high temperature diamond crystallization characteristics

Received: 06 May 2020
Revised: 28 May 2020
Accepted manuscript online: 05 June 2020

PACS:	92.60.hv	(Pressure, density, and temperature)
	81.05.ug	(Diamond)
	81.10.-h	(Methods of crystal growth; physics and chemistry of crystal growth, crystal morphology, and orientation)
	61.72.jn	(Color centers)

Fund: Project supported by the National Natural Science Foundation of China (Grant No. 11604246), Natural Science Foundation of Guizhou Province Education Department of China (Grant Nos. KY2017053 and KY2018343), Natural Science Foundation of Guizhou Procince Science and Technology Agency of China (Grant Nos. 20181163 and LH 20177311), and Outstanding Young Science and Technology Talents of Guizhou Pronice of China (Grant No. 20195673).

Corresponding Authors: Yong Li
E-mail: likaiyong6@163.com

Cite this article:

Yong Li(李勇), Debing Tan(谭德斌), Qiang Wang(王强), Zhengguo Xiao(肖政国), Changhai Tian(田昌海), Lin Chen(陈琳) Crystallization and characteristics of {100}-oriented diamond with CH₄N₂S additive under high pressure and high temperature 2020 Chin. Phys. B 29 098103

[1]	Guo M M, Li S S, Hu M H, Su T C, Wang J Z, Gao G J, You Y and Nie Y 2020 Chin. Phys. B 29 018101
[2]	Li Y, Li Y D, Wang Y, Zhang J, Song M S, She Y C and Chen X Z 2018 Cryst. Eng. Comm. 20 4127
[3]	Angerer A, Streltsov K, Astner T, Putz S, Sumiya H, Onoda S, Isoya J, Munro W J, Nemoto K, Schmiedmayer J and Majer J 2018 Nat. Phys. 14 1168
[4]	Dutt M V G, Childress L, Jiang L, Togan E, Maze J, Jelezko F, Zibrov A S, Hemmer P R and Lukin M D 2007 Science 316 1312
[5]	Maze J R, Stanwix P L, Hodges J S, Hong S, Taylor J M, Cappellaro P, Jiang L, Zibrov A S, Yacoby A, Walsworth R L and Lukin M D 2008 Nature 455 644
[6]	Zhang J F, Yang P Z, Ren Z Y, Zhang J C, Xu S R, Zhang C F, Xu L and Hao Y 2018 Acta Phys. Sin. 67 068101 (in Chinese)
[7]	Xu H, Liu J J, Ye H T, Coathup D J, Khomich A V and Hu X J 2018 Chin. Phys. B 27 096104
[8]	Hu M H, Bi N, Li S S, Su T C, Hu Q, Jia X P and Ma H A 2015 Chin. Phys. B 24 038101
[9]	Wang J Z, Li S S, Hu M H, Su T C, Gao G J, Guo M M, You Y and Nie Y 2020 Int. J. Refract. Met. Hard Mater. 87 105150
[10]	Briddon P R and Jones R 1993 Physica B 185 179
[11]	Salustro S, Ferrari A M, Gentile F S, Denmarais J K and Rérat M 2018 J. Phys. Chem. A 122 594
[12]	Sutherland G B B M, Blackwell D E and Simeral W G 1954 Nature 174 901
[13]	Li Y, Jia X P, Hu M H, Yan B M, Zhou Z X, Fang C, Zhang Z F and Ma H A 2012 Int. J. Refract. Met. Hard Mater. 34 27
[14]	Guo L S, Ma H A, Chen L C, Chen N, Miao X Y, Wang Y, Fang S, Yang Z Q, Fang C and Jia X P 2018 Cryst. Eng. Comm. 20 5457
[15]	Li Y, Jia X P, Yan B M, Zhou Z X, Fang C, Zhang Z F, Sun S S and Ma H A 2012 Journal of Crystal Growth 359 49
[16]	Pal'yanov Y N, Kupriyanov I N, Borzdov Y M, Sokol A G and Khokhryakov A F 2009 Cryst. Growth Des. 9 2922
[17]	Meng Y F, Yan C S, Lai J, Krasnicki S, Shu H Y, Yu T, Liang Q, Mao H K and Hemley Russell J 2008 Proc. Acad. Natl. Sci. USA 105 17620
[18]	Akaishi M, Handa H, Sato Y, Setaka N, Ohsawa T and Fukunaga O 1982 J. Mater. Sci. 17 193
[19]	Fuchs F, Wild C, Schwarz K and Koidl P 1995 Diam. Relat. Mater. 4 652
[20]	Li Y, Jia X P, Hu M H, Liu X B, Yan B M, Zhou Z X, Zhang Z F and Ma H A 2012 Chin. Phys. B 21 058101
[21]	Huang G F, Jia X P, Yin J W, Ma H A and Zheng Y J 2013 Int. J. Refractory Metals and Hard Mater 41 517
[22]	Liu X B, Jia X P, Fang C and Ma H A 2016 Cryst. Eng. Comm. 18 8506
[23]	Chen N, Ma H A, Yan B M, Chen L C, Chen L X, Guo L S, Miao X Y, Fang C and Jia X P 2018 Cryst. Growth Des. 18 3870
[24]	Mainwood A 1994 Phys. Rev. B 49 7934
[25]	Li Y, Li S S, She Y C and Guan X M 2017 Journal of Synthetic Crystals 46 778 (in Chinese)
[26]	Lindblom J, Hölsä J, Papunen H and Häkkänen H 2005 American Mineralogist 90 428
[27]	Stanwix P L, Pham L M, Maze J R, Le Sage D, Yeung T K, Cappelllaro P, Hemmer P R, Yacoby, Lukin M D and Walsworth R L 2010 Phys. Rev. B 82 201201
[28]	Chen L C, Miao X Y, Ma H A, Guo L S, Wang Z K, Yang Z Q, Fang C and Jia X P 2018 Cryst. Eng. Comm. 20 7164
[29]	Rabeau J R, Chin Y L, Prawer S, Jelezko F, Gaebel T and Wrachtrup J 2005 Appl. Phys. Lett. 86 131926

[1]	Adaptive genetic algorithm-based design of gamma-graphyne nanoribbon incorporating diamond-shaped segment with high thermoelectric conversion efficiency Jingyuan Lu(陆静远), Chunfeng Cui(崔春凤), Tao Ouyang(欧阳滔), Jin Li(李金), Chaoyu He(何朝宇), Chao Tang(唐超), and Jianxin Zhong(钟建新). Chin. Phys. B, 2023, 32(4): 048401.
[2]	A 4H-SiC trench IGBT with controllable hole-extracting path for low loss Lijuan Wu(吴丽娟), Heng Liu(刘恒), Xuanting Song(宋宣廷), Xing Chen(陈星), Jinsheng Zeng(曾金胜), Tao Qiu(邱滔), and Banghui Zhang(张帮会). Chin. Phys. B, 2023, 32(4): 048503.
[3]	Suppression and compensation effect of oxygen on the behavior of heavily boron-doped diamond films Li-Cai Hao(郝礼才), Zi-Ang Chen(陈子昂), Dong-Yang Liu(刘东阳), Wei-Kang Zhao(赵伟康),Ming Zhang(张鸣), Kun Tang(汤琨), Shun-Ming Zhu(朱顺明), Jian-Dong Ye(叶建东),Rong Zhang(张荣), You-Dou Zheng(郑有炓), and Shu-Lin Gu(顾书林). Chin. Phys. B, 2023, 32(3): 038101.
[4]	A simulation study of polarization characteristics of ultrathin CsPbBr₃ nanowires with different cross-section shapes and sizes Kang Yang(杨康), Huiqing Hu(胡回清), Jiaojiao Wang(王娇娇), Lingling Deng(邓玲玲), Yunqing Lu(陆云清), and Jin Wang(王瑾). Chin. Phys. B, 2023, 32(2): 024214.
[5]	Generation of a blue-detuned optical storage ring by a metasurface and its application in optical trapping of cold molecules Chen Ling(凌晨), Yaling Yin(尹亚玲), Yang Liu(刘泱), Lin Li(李林), and Yong Xia(夏勇). Chin. Phys. B, 2023, 32(2): 023301.
[6]	In situ study of calcite-III dimorphism using dynamic diamond anvil cell Xia Zhao(赵霞), Sheng-Hua Mei(梅升华), Zhi Zheng(郑直), Yue Gao(高悦), Jiang-Zhi Chen(陈姜智), Yue-Gao Liu(刘月高), Jian-Guo Sun(孙建国), Yan Li(李艳), and Jian-Hui Sun(孙建辉). Chin. Phys. B, 2022, 31(9): 096201.
[7]	Numerical simulation of the thermal non-equilibrium flow-field characteristics of a hypersonic Apollo-like vehicle Minghao Yu(喻明浩)^†, Zeyang Qiu(邱泽洋), Bo Lv(吕博), and Zhe Wang(王哲). Chin. Phys. B, 2022, 31(9): 094702.
[8]	Determination of band alignment between GaO_x and boron doped diamond for a selective-area-doped termination structure Qi-Liang Wang(王启亮), Shi-Yang Fu(付诗洋), Si-Han He(何思翰), Hai-Bo Zhang(张海波),Shao-Heng Cheng(成绍恒), Liu-An Li(李柳暗), and Hong-Dong Li(李红东). Chin. Phys. B, 2022, 31(8): 088104.
[9]	In-situ ultrasonic calibrations of pressure and temperature in a hinge-type double-stage cubic large volume press Qingze Li(李青泽), Xiping Chen(陈喜平), Lei Xie(谢雷), Tiexin Han(韩铁鑫), Jiacheng Sun(孙嘉程), and Leiming Fang(房雷鸣). Chin. Phys. B, 2022, 31(6): 060702.
[10]	Synergistic influences of titanium, boron, and oxygen on large-size single-crystal diamond growth at high pressure and high temperature Guang-Tong Zhou(周广通), Yu-Hu Mu(穆玉虎), Yuan-Wen Song(宋元文), Zhuang-Fei Zhang(张壮飞), Yue-Wen Zhang(张跃文), Wei-Xia Shen(沈维霞), Qian-Qian Wang(王倩倩), Biao Wan(万彪), Chao Fang(房超), Liang-Chao Chen(陈良超), Ya-Dong Li(李亚东), and Xiao-Peng Jia(贾晓鹏). Chin. Phys. B, 2022, 31(6): 068103.
[11]	Investigating the thermal conductivity of materials by analyzing the temperature distribution in diamond anvils cell under high pressure Caihong Jia(贾彩红), Min Cao(曹敏), Tingting Ji(冀婷婷), Dawei Jiang(蒋大伟), and Chunxiao Gao(高春晓). Chin. Phys. B, 2022, 31(4): 040701.
[12]	Effect of nonlinear translations on the pulsation of cavitation bubbles Lingling Zhang(张玲玲), Weizhong Chen(陈伟中), Yang Shen(沈阳), Yaorong Wu(武耀蓉), Guoying Zhao(赵帼英), and Shaoyang Kou(寇少杨). Chin. Phys. B, 2022, 31(4): 044303.
[13]	Dependence of nitrogen vacancy color centers on nitrogen concentration in synthetic diamond Yong Li(李勇), Xiaozhou Chen(陈孝洲), Maowu Ran(冉茂武), Yanchao She(佘彦超), Zhengguo Xiao(肖政国), Meihua Hu(胡美华), Ying Wang(王应), and Jun An(安军). Chin. Phys. B, 2022, 31(4): 046107.
[14]	Effect of oxygen on regulation of properties of moderately boron-doped diamond films Dong-Yang Liu(刘东阳), Li-Cai Hao(郝礼才), Wei-Kang Zhao(赵伟康), Zi-Ang Chen(陈子昂), Kun Tang(汤琨), Shun-Ming Zhu(朱顺明), Jian-Dong Ye(叶建东), Rong Zhang(张荣), You-Dou Zheng(郑有炓), and Shu-Lin Gu(顾书林). Chin. Phys. B, 2022, 31(12): 128104.
[15]	Origin, characteristics, and suppression of residual nitrogen in MPCVD diamond growth reactor Yan Teng(滕妍), Dong-Yang Liu(刘东阳), Kun Tang(汤琨), Wei-Kang Zhao(赵伟康), Zi-Ang Chen(陈子昂), Ying-Meng Huang(黄颖蒙), Jing-Jing Duan(段晶晶), Yue Bian(卞岳), Jian-Dong Ye(叶建东), Shun-Ming Zhu(朱顺明), Rong Zhang(张荣), You-Dou Zheng(郑有炓), and Shu-Lin Gu(顾书林). Chin. Phys. B, 2022, 31(12): 128106.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Metrics
Related Articles

Crystallization and characteristics of {100}-oriented diamond with CH4N2S additive under high pressure and high temperature

Cite this article:

Online attention

Crystallization and characteristics of {100}-oriented diamond with CH₄N₂S additive under high pressure and high temperature