Abstract Amorphous-layer-free nanocrystalline silicon films were prepared by a very high frequency plasma enhanced chemical vapor deposition (PECVD) technique using hydrogen-diluted SiH4 at 250 ℃. The dependence of the crystallinity of the film on the hydrogen dilution ratio and the film thickness was investigated. Raman spectra show that the thickness of the initial amorphous incubation layer on silicon oxide gradually decreases with increasing hydrogen dilution ratio. High-resolution transmission electron microscopy reveals that the initial amorphous incubation layer can be completely eliminated at a hydrogen dilution ratio of 98%, which is lower than that needed for the growth of amorphous-layer-free nanocrystalline silicon using an excitation frequency of 13.56 MHz. More studies on the microstructure evolution of the initial amorphous incubation layer with hydrogen dilution ratios were performed using Fourier-transform infrared spectroscopy. It is suggested that the high hydrogen dilution, as well as the higher plasma excitation frequency, plays an important role in the formation of amorphous-layer-free nanocrystalline silicon films.
Fund: Project supported by the National Natural Science Foundation of China (Grant No. 60806046), the Natural Science Foundation of Guangdong Province of China (Grant No. S2011010001853), and the FDYT (Grant No. LYM10099).
Guo Yan-Qing(郭艳青), Huang Rui(黄锐), Song Jie(宋捷), Wang Xiang(王祥), Song Chao(宋超), and Zhang Yi-Xiong(张奕雄) Growth characteristics of amorphous-layer-free nanocrystalline silicon films fabricated by very high frequency PECVD at 250 ℃ 2012 Chin. Phys. B 21 066106
[1]
Zhang X D, Zheng X X, Xu S Z, Lin Q, Wei C C, Sun J, Geng X H and Zhao Y 2011 Chin. Phys. B 20 108801
[2]
Chen K J, Huang X F, Xu J and Feng D 1992 Appl. Phys. Lett. 61 2069
[3]
Shi Y, Saito K, Ishikuro H and Hiramoto T 1998 J. Appl. Phys. 84 2358
[4]
Peng W B, Liu S Y, Xiao H B, Zhang C S, Shi M J, Zeng X B, Xu Y Y, Kong G L and Yu Y D 2009 Acta Phys. Sin. 58 5716 (in Chinese)
[5]
Huang R, Lin X Y, Huang W Y, Yao R H, Yu Y P, Lin K X, Wei J H and Zhu Z S 2006 Thin Solid Films 513 380
[6]
Xu J, Chen K J, Feng D, Miyazaki S and Hirose M 1996 Solid State Commun. 99 269
[7]
Klein S, Finger F, Carius R and Stutzmann M 2005 J. Appl. Phys. 98 024905
[8]
Kocka J, Mates T, Stuchlíkov? H, Stuchlík J and Fejfar A 2006 Thin Solid Films 501 107
[9]
Matsuda A 2004 J. Non-Cryst. Solids 338-340 1
[10]
Vallat-Sauvain E, Kroll U, Meier J, Shah A and Pohl J 2000 J. Appl. Phys. 87 3137
[11]
Hou G F, Xue J M, Guo Q C, Sun J, Zhao Y, Geng X H and Li Y G 2007 Chin. Phys. 16 553
[12]
Li J, Wang J, Yin M, Gao P, Chen Q, Li Y and He D 2008 J. Cryst. Growth 310 4340
[13]
Chen Y S, Xu Y H, Gu J H, Lu J X, Yang S E and Gao X Y 2010 Chin. Phys. B 19 087206
[14]
Danesh P, Pantchev B, Grambole D and Schmidt B 2002 Appl. Phys. Lett. 80 2463
[15]
Gordijn A, Rath J K and Schropp R E I 2004 Appl. Phys. Lett. 85 5096
[16]
Song J, Guo Y Q, Wang X, Ding H L and Huang R 2010 Acta Phys. Sin. 59 7378 (in Chinese)
[17]
Park Y B and Rhee S W 2001 J. Appl. Phys. 90 217
[18]
Zhou J H, Ikuta K, Yasuda T, Umeda T, Yamasaki S and Tanaka K 1997 Appl. Phys. Lett. 71 1534
[19]
Han D X, Wang K, Owens J M, Gedvilas L, Nelson B, Habuchi H and Tanaka M 2003 J. Appl. Phys. 93 3776
[20]
Vetterl O, Hapke P, Houben L, Finger F, Carius R and Wagner H 1999 J. Appl. Phys. 85 2991
[21]
Amanatides E, Hammad A, Katsia E and Mataras D 2005 J. Appl. Phys. 97 073303
Altmetric calculates a score based on the online attention an article receives. Each coloured thread in the circle represents a different type of online attention. The number in the centre is the Altmetric score. Social media and mainstream news media are the main sources that calculate the score. Reference managers such as Mendeley are also tracked but do not contribute to the score. Older articles often score higher because they have had more time to get noticed. To account for this, Altmetric has included the context data for other articles of a similar age.