Abstract Er$^{3+}$- and Er$^{3+}$/Yb$^{3+}$-doped lead germanate glasses that are suitable for use in fibre lasers and optical amplifiers as well as optical waveguide devices have been fabricated and characterized. The absorption spectra from near-infrared to visible were obtained and the Judd-Ofelt parameters were determined from the absorption band. Intense and broad 1.53μm infrared fluorescence and visible upconversion luminescence were observed under 976 nm diode laser excitation. For 1.53μm emission band, the full widths at half-maximum are 36, 37, 51 nm for GPE, GPYE and GPFE samples, respectively. For frequency upconversion emission, the intense bands centred at around 524, 545, 657nm are due to the $^4$S$_{3/2}$+$^2$H$_{11/2}$→$^4$I$_{15/2}$ and $^4$F$_{9/2}$→$^4$I$_{15/2}$ transitions of Er$^{3+}$ ions. The quadratic dependence of the green and red emissions on excitation power indicates that the two-photon absorption process occurs under the 976nm excitation.
Received: 30 June 2003
Revised: 18 August 2003
Accepted manuscript online:
Fund: Project supported by the National Natural Science Foundations of China (Grant Nos 60307004 and 60207006) and the Fund of Optical Science and Technology of Shanghai (Grant No 022261046).
Cite this article:
Yang Zhong-Min (杨中民), Xu Shi-Qing (徐时清), Hu Li-Li (胡丽丽), Jiang Zhong-Hong (姜中宏) Optical transitions in Er3+ doped lead germanate glasses 2004 Chinese Physics 13 401
Altmetric calculates a score based on the online attention an article receives. Each coloured thread in the circle represents a different type of online attention. The number in the centre is the Altmetric score. Social media and mainstream news media are the main sources that calculate the score. Reference managers such as Mendeley are also tracked but do not contribute to the score. Older articles often score higher because they have had more time to get noticed. To account for this, Altmetric has included the context data for other articles of a similar age.