Studies on organic binders with high infrared transparency

Fu Cheng-Wu(傅成武), Zhou Hao-Shen(周豪慎), and Chen Ming-Qing(陈明清)
School of Chemical and Material Engineering, Jiangnan University, Wuxi 214122, China
Abstract  This paper reports that two kinds of polymers with high infrared transparency and good mechanical and physical properties have been prepared. An internal standard method is used to evaluate the infrared transparency of the binders. The physical and mechanical properties of the binders are measured according to corresponding standards. The results show the absorbance of polymer A in 8--14 μm range is 26% that of the ethylene-vinyl acetate copolymer (EVA), and polymer B is 9% that of the EVA correspondingly. The film of polymer A shows good flexibility of above 1 mm, a hardness of grade 1, and adhesion of grade 2. The film of polymer B shows good flexibility of above 1 mm, a hardness of grade 1, and adhesion of grade 1.
Keywords:  infrared transparency      adhesion      hardness      internal standard  
Received:  12 January 2009      Revised:  11 February 2009      Accepted manuscript online: 
PACS:  78.30.Jw (Organic compounds, polymers)  
  78.66.Qn (Polymers; organic compounds)  
  62.20.Qp (Friction, tribology, and hardness)  
  81.40.Np (Fatigue, corrosion fatigue, embrittlement, cracking, fracture, and failure)  
  82.35.Gh (Polymers on surfaces; adhesion)  
  81.05.Lg (Polymers and plastics; rubber; synthetic and natural fibers; organometallic and organic materials)  
Fund: Project supported by the National Natural Science Foundation of China (Grant No 20671043).

Cite this article: 

Fu Cheng-Wu(傅成武), Zhou Hao-Shen(周豪慎), and Chen Ming-Qing(陈明清) Studies on organic binders with high infrared transparency 2009 Chin. Phys. B 18 3061

[1] Microstructure and hardening effect of pure tungsten and ZrO2 strengthened tungsten under carbon ion irradiation at 700℃
Chun-Yang Luo(罗春阳), Bo Cui(崔博), Liu-Jie Xu(徐流杰), Le Zong(宗乐), Chuan Xu(徐川), En-Gang Fu(付恩刚), Xiao-Song Zhou(周晓松), Xing-Gui Long(龙兴贵), Shu-Ming Peng(彭述明), Shi-Zhong Wei(魏世忠), and Hua-Hai Shen(申华海). Chin. Phys. B, 2022, 31(9): 096102.
[2] Structure, phase evolution and properties of Ta films deposited using hybrid high-power pulsed and DC magnetron co-sputtering
Min Huang(黄敏), Yan-Song Liu(刘艳松), Zhi-Bing He(何智兵), and Yong Yi(易勇). Chin. Phys. B, 2022, 31(6): 066101.
[3] Properties of B4C-TiB2 ceramics prepared by spark plasma sintering
Jingzhe Fan(范静哲), Weixia Shen(沈维霞), Zhuangfei Zhang(张壮飞, Chao Fang(房超), Yuewen Zhang(张跃文), Liangchao Chen(陈良超), Qianqian Wang(王倩倩), Biao Wan(万彪), and Xiaopeng Jia(贾晓鹏). Chin. Phys. B, 2021, 30(3): 038105.
[4] Molecular simulation study of the adhesion work for water droplets on water monolayer at room temperature
Mengyang Qu(屈孟杨), Bo Zhou(周波), and Chunlei Wang(王春雷). Chin. Phys. B, 2021, 30(10): 106804.
[5] Progress in functional studies of transition metal borides
Teng Ma(马腾), Pinwen Zhu(朱品文), and Xiaohui Yu(于晓辉). Chin. Phys. B, 2021, 30(10): 108103.
[6] Nanosheet-structured B4C with high hardness up to 42 GPa
Chang-Chun Wang(王常春), Le-Le Song(宋乐乐). Chin. Phys. B, 2019, 28(6): 066201.
[7] High-pressure dynamic, thermodynamic properties, and hardness of CdP2
Shi-Quan Feng(冯世全), Ling-Li Wang(王伶俐), Xiao-Xu Jiang(姜晓旭), Hai-Nin Li(李海宁), Xin-Lu Cheng(程新路), Lei Su(苏磊). Chin. Phys. B, 2017, 26(4): 046301.
[8] Theoretical calculations of hardness and metallicity for multibond hexagonal 5d transition metal diborides with ReB2 structure
Jun Yang(杨俊), Fa-Ming Gao(高发明), Yong-Shan Liu(刘永山). Chin. Phys. B, 2017, 26(10): 106202.
[9] New ordered MAX phase Mo2TiAlC2: Elastic and electronic properties from first-principles
M A Hadi, M S Ali. Chin. Phys. B, 2016, 25(10): 107103.
[10] Stability of focal adhesion enhanced by its inner force fluctuation
Mao Zhi-Xiu (毛志秀), Chen Xiao-Feng (陈笑风), Chen Bin (陈彬). Chin. Phys. B, 2015, 24(8): 088702.
[11] Effect of deposition parameters on structural and mechanicalproperties of niobium nitride synthesized by plasma focus device
Jamil Siddiqui, Tousif Hussain, Riaz Ahmad, Nida Khalid. Chin. Phys. B, 2015, 24(6): 065204.
[12] Stability and elastic properties of NbxCy compounds
Gao Xu-Peng (高旭鹏), Jiang Ye-Hua (蒋业华), Liu Yang-Zhen (刘洋赈), Zhou Rong (周荣), Feng Jing (冯晶). Chin. Phys. B, 2014, 23(9): 097704.
[13] Preparation and characterization of thick cubic boron nitride films
Wang Ming-E (王明娥), Ma Guo-Jia (马国佳), Dong Chuang (董闯), Gong Shui-Li (巩水利). Chin. Phys. B, 2014, 23(6): 066805.
[14] Elastic and thermodynamic properties of vanadium nitride under pressure and the effect of metallic bonding on its hardness
Pu Chun-Ying (濮春英), Zhou Da-Wei (周大伟), Bao Dai-Xiao (包代小), Lu Cheng (卢成), Jin Xi-Lian (靳希联), Su Tai-Chao (宿太超), Zhang Fei-Wu (张飞武). Chin. Phys. B, 2014, 23(2): 026201.
[15] First-principles calculations on Si (220) located 6H-SiC (1010) surface with different stacking sites
He Xiao-Min (贺小敏), Chen Zhi-Ming (陈治明), Pu Hong-Bin (蒲红斌), Li Lian-Bi (李连碧), Huang Lei (黄磊). Chin. Phys. B, 2014, 23(10): 106802.
No Suggested Reading articles found!