Abstract Structure, magnetic and transport properties of YMn6Sn6-xGax (0≤x≤0.6) compounds with a HfFe6Ge6-type structure were investigated. It was found that the Ga substitution leads to a contraction of the unit-cell volume. A transition from an antiferromagnetic to a ferromagnetic (or ferrimagnetic) state can be observed for samples (0.1≤x≤0.2) with increasing temperature. The antiferro-ferromagnetic transition for samples with x≤0.2 can also be induced by an external field. The required field is very low, and decreases with increasing Ga concentration. More Ga concentration (x≥0.3) leads to the samples being ferromagnetic in the whole temperature range below the Curie temperature. The Ga substitution weakens the interlayer magnetic coupling between the Mn spins. Corresponding to the metamagnetic transition, a magnetoresistance as large as 32% under a field of 5 T was observed at 5 K for the sample with x=0.2.
Received: 23 November 2000
Accepted manuscript online:
Altmetric calculates a score based on the online attention an article receives. Each coloured thread in the circle represents a different type of online attention. The number in the centre is the Altmetric score. Social media and mainstream news media are the main sources that calculate the score. Reference managers such as Mendeley are also tracked but do not contribute to the score. Older articles often score higher because they have had more time to get noticed. To account for this, Altmetric has included the context data for other articles of a similar age.