Abstract This paper reports that the nickel--silicone rubber composites with enhanced piezoresistivity were synthesized with much reduced nickel concentration. A large piezosensitivity of 0.716/kPa and a gauge factor of 600 have been obtained for a composite sample with filler-polymer ratio of 2.7:1 by weight. Measurements of resistance as a function of uniaxial force reveal that the piezoresistance arises predominantly from the internal heterogeneity of the material and the effect of geometrical changes of samples under pressure is neglectably small. The nonlinear current--voltage characteristic of the composite depends strongly on the filler content, the initial compression and the electrical current flowing in the sample. Ohmic behaviour has been observed only in the highly compressed samples. The breakdown strength decreases with increasing filler content of the composite. Both I-V and R-f characteristics indicates that the resistivity of the composites decreases with electrical field, suggesting that the composite may also be used to make voltage sensitive resistors for protecting circuits. All the experimental results favour a quantum tunnelling mechanism of conductivity. It finds that the concept `negative resistance', often used to describe the phenomena that current decreases with increasing voltage, is not appropriate and should be avoided.
Received: 11 August 2008
Revised: 31 August 2008
Accepted manuscript online:
PACS:
72.20.Fr
(Low-field transport and mobility; piezoresistance)
(Reinforced polymers and polymer-based composites)
Fund: Project
supported by National Natural Science Foundation of China (Grant No
60571063), and partially sponsored by the Scientific Research
Foundation for the Returned Overseas Chinese
Scholars, State Education Ministry.
Cite this article:
Chang Fang-Gao(常方高), Yang Feng(杨枫), Wang Shao-Xiang(王少祥), Zhang Na(张娜), and Song Gui-Lin(宋桂林) Enhanced piezoresistivity in Ni--silicone rubber composites 2009 Chin. Phys. B 18 652
Altmetric calculates a score based on the online attention an article receives. Each coloured thread in the circle represents a different type of online attention. The number in the centre is the Altmetric score. Social media and mainstream news media are the main sources that calculate the score. Reference managers such as Mendeley are also tracked but do not contribute to the score. Older articles often score higher because they have had more time to get noticed. To account for this, Altmetric has included the context data for other articles of a similar age.