Uncovering the internal structure of five-fold twinned nanowires through 3D electron diffraction mapping |
Xin Fu(付新)1,2,3,4 |
1 GRINM Group Corporation Limited, National Analysis and Testing Center for Nonferrous Metals and Electronic Materials, Beijing 101400, China; 2 Guobiao(Beijing) Testing & Certification Co., Ltd., Beijing 101400, China; 3 China United Test&Certification Co., Ltd., Beijing 101400, China; 4 General Research Institute for Nonferrous Metals, Beijing 100088, China |
|
|
Abstract Five-fold twinned nanostructures are intrinsically strained or relaxed by extended defects to satisfy the space-filling requirement. Although both of metallic and semiconductor five-fold twinned nanostructures show inhomogeneity in their cross-sectional strain distribution, the evident strain concentration at twin boundaries in the semiconductor systems has been found in contrast to the metallic systems. Naturally, a problem is raised how the chemical bonding characteristics of various five-fold twinned nanosystems affects their strain-relieving defect structures. Here using three-dimensional (3D) electron diffraction mapping methodology, the intrinsic strain and the strain-relieving defects in a pentagonal Ag nanowire and a star-shaped boron carbide nanowire, both of them have basically equal radial twin-plane width about 30 nm, are non-destructively characterized. The non-uniform strain and defect distribution between the five single crystalline segments are found in both of the five-fold twinned nanowires. Diffraction intensity fine structure analysis for the boron carbide five-fold twinned nanowire indicates the presence of high-density of planar defects which are responsible for the accommodation of the intrinsic angular excess. However, for the Ag five-fold twinned nanowire, the star-disclination strain field is still present, although is partially relieved by the formation of localized stacking fault layers accompanied by partial dislocations. Energetic analysis suggests that the variety in the strain-relaxation ways for the two types of five-fold twinned nanowires could be ascribed to the large difference in shear modulus between the soft noble metal Ag and the superhard covalent compound boron carbide.
|
Received: 15 January 2020
Revised: 02 March 2020
Accepted manuscript online:
|
PACS:
|
81.07.-b
|
(Nanoscale materials and structures: fabrication and characterization)
|
|
Fund: Project supported by the National Natural Science Foundation of China (Grant Nos. 51201015 and U1532262). |
Corresponding Authors:
Xin Fu
E-mail: fuxints@126.com
|
Cite this article:
Xin Fu(付新) Uncovering the internal structure of five-fold twinned nanowires through 3D electron diffraction mapping 2020 Chin. Phys. B 29 068101
|
[1] |
Hofmeister H 2004 Encyclopedia of Nanoscience and Nanotechnology, Nalwa H S ed. (American Scientific Publishers) pp. 431-452
|
[2] |
Liu S, Wang X Z, Tao H, Li T, Qi L, Xu Z, Fu X Z and Luo J L 2018 Nano Energy 45 456
|
[3] |
Yu R, Wu H, Wang J D and Zhu J 2017 ACS Appl. Mater. Interf. 9 4253
|
[4] |
Fu X, Jiang J, Liu C and Yuan J 2009 Nanotechnology 20 365707
|
[5] |
Jiang J, Cao M H, Sun Y K, Wu P W and Yuan J 2006 Appl. Phys. Lett. 88 163107
|
[6] |
Gryaznov V G, Heydenreich J, Kaprelov A M, Nepijko S A, Romanov A E and Urban J 1999 Cryst. Res. Technol. 34 1091
|
[7] |
Wu B, Heidelberg A, Boland J J, Sader J E, Sun X and Li Y 2006 Nano Lett. 6 468
|
[8] |
Zhu Y, Qin Q, Xu F, Fan F, Ding Y, Zhang T, J Wiley B and Wang Z 2012 Phys. Rev. B 85 045443
|
[9] |
Pietrobon B, McEachran M and Kitaev V 2009 ACS Nano 3 21
|
[10] |
Bian T, Zhang H, Jiang Y, Jin C, Wu J, Yang H and Yang D 2015 Nano Lett. 15 7808
|
[11] |
De Wit R 1972 J. Phys. C: Solid State Phys. 5 529
|
[12] |
Niekiel F, Bitzek E and Spiecker E 2014 ACS Nano 8 1629
|
[13] |
Johnson C L, Snoeck E, Ezcurdia M, Rodriguez-Gonzalez B, Pastoriza-Santos I, Liz-Marzan L M and Hytch M J 2008 Nat. Mater. 7 120
|
[14] |
Fu X, Jiang J, Zhang W and Yuan J 2008 Appl. Phys. Lett. 93 043101
|
[15] |
Zhang W, Liu Y, Cao R, Li Z, Zhang Y, Tang Y and Fan K 2008 J. Am. Chem. Soc. 130 15581
|
[16] |
Song M, Wu Z, Lu N and Li D 2019 Chem. Mater. 31 842
|
[17] |
Chen H Y, Gao Y, Yu H C, Zhang H R, Liu L B, Shi Y G, Tian H F, Xie S S and Li J Q 2004 Micron 35 469
|
[18] |
Fu X and Yuan J 2017 Sci. Rep. 7 6206
|
[19] |
Kim J W, Ulvestad A, Manna S, Harder R, Fullerton E E and Shpyrko O G 2017 Nanoscale 9 13153
|
[20] |
Zhu L, Shen X, Zeng Z, Wang H, Zhang H and Chen H 2012 ACS Nano 6 6033
|
[21] |
Fu X and Yuan J 2013 Nanoscale 5 9067
|
[22] |
Marks L D 1994 Rep. Prog. Phys. 57 603
|
[23] |
Iijima S 1987 Jpn. J. Appl. Phys. 26 365
|
[24] |
Pei Y T and De Hosson J T M 2001 Acta Mater. 49 561
|
[25] |
Midgley P A and Dunin-Borkowski R E 2009 Nat. Mater. 8 271
|
[26] |
Xia Y, Xiong Y, Lim B and Skrabalak S E 2009 Angew. Chem. Int. Ed. 48 60
|
[27] |
Schmidt V, Wittemann J V, Senz S and Goesele U 2009 Adv. Mater. 21 2681
|
[28] |
Allen J E, Hemesath E R, Perea D E, Lensch-Falk J L, Li Z Y, Yin F, Gass M H, Wang P, Bleloch A L and Palmer R E 2008 Nat. Nanotechnol. 3 168
|
[29] |
Xing Y, Yu D, Xi Z and Xue Z 2002 Chin. Phys. 11 1047
|
[30] |
Fu X and Yuan J 2014 J. Phys.: Conf. Ser. 522 012064
|
[31] |
Fu X and Yuan J 2011 J. Chin. Electron. Microsc. Soc. 30 439
|
[32] |
Sun Y, Ren Y, Liu Y, Wen J, Okasinski J S and Miller D J 2012 Nat. Commun. 3 971
|
[33] |
Zhou Y and Fichthorn K A 2014 J. Phys. Chem. C 118 18746
|
[34] |
McCarthy E K, Bellew A T, Sader J E and Boland J J 2014 Nat. Commun. 5 4336
|
[35] |
Dodd S P, Saunders G A and James B 2002 J. Mater. Sci. 37 2731
|
[36] |
Tao X, Dong L, Wang X, Zhang W, Nelson B J and Li X 2010 Adv. Mater. 22 2055
|
[37] |
Yu Z Y, Fu X and Zhu J 2011 Sci. Chin. (Technol. Sci.) 54 2119
|
[38] |
Ashbee K H G 1971 Acta Metall. 19 1079
|
[39] |
Murr L E 1975 Interfacial phenomena in metals and alloys (Addison-Wesley Educational Publishers Inc.)
|
[40] |
Meyer R and Lewis L J 2002 Phys. Rev. B 66 052106
|
[41] |
Narayanan S, Cheng G, Zeng Z, Zhu Y and Zhu T 2015 Nano Lett. 15 4037
|
[42] |
Qin Q, Yin S, Cheng G, Li X, Chang T H, Richter G, Zhu Y and Gao H 2015 Nat. Commun. 6 5983
|
[43] |
Patala S, Marks L D and Cruz M O D L 2013 J. Phys. Chem. C 117 1485
|
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
Altmetric
|
blogs
Facebook pages
Wikipedia page
Google+ users
|
Online attention
Altmetric calculates a score based on the online attention an article receives. Each coloured thread in the circle represents a different type of online attention. The number in the centre is the Altmetric score. Social media and mainstream news media are the main sources that calculate the score. Reference managers such as Mendeley are also tracked but do not contribute to the score. Older articles often score higher because they have had more time to get noticed. To account for this, Altmetric has included the context data for other articles of a similar age.
View more on Altmetrics
|
|
|