Multiscale modeling of droplet deposition and solidification dendrite growth during DED-Arc additive manufacturing of a nickel-based superalloy

Qingyu Zhang(张庆宇)1, Zhixian Chen(陈志贤)1, Rong Wang(王荣)1, Pengcheng Huan(环鹏程)2, Dongke Sun(孙东科)3, and Xiaonan Wang(王晓南)1,†
1 School of Metallic Materials and Advanced Manufacturing, Soochow University, Suzhou 215137, China;
2 School of Automotive Engineering, Suzhou University of Technology, Suzhou 215500, China;
3 School of Mechanical Engineering, Southeast University, Nanjing 211189, China
Abstract  The evolutions of droplet morphology on the macroscale and solidification microstructure on the microscale, during direct energy deposition (DED)-Arc additive manufacturing of a nickel-based alloy, are simulated by developing a multiscale model based on the lattice Boltzmann and cellular automaton models. The macroscopic model is quantitatively validated by modeling the time-dependent phase interface position and temperature distribution for a classical Stefan problem of phase change in the multiphase system. In the simulation of droplet deposition, it is found that the contact line length between the deposited droplet and substrate is proportional to a defined overall factor, $d_{\rm D}^{2} \cdot \left| {{{\bm u}}} \right|^{2}\cdot \Delta T\cdot \left( {1+\cos \theta_{0} } \right)$, composed of droplet size ($d_{\rm D}$), impact velocity ($\bm u$), temperature difference ($\Delta T$), and intrinsic contact angle ($\theta$), respectively. The overall factor allows one to evaluate the contact line length prior to the experiment, which is significant for heat transfer efficiency and formability of the additive manufacturing products. The evolution of temperature distribution during multilayer droplet deposition is obtained, and the calculated cooling rate ($\sim 800 $ K/s) and temperature gradient ($\sim 1 $ K/m) accord well with the typical data in the literature. By mapping the macroscopic temperature field data into the microscopic model through multidimensional linear interpolation, the growth of dendrites during solidification of the pillar-shaped product is reproduced. Both the simulation and experimental results show that the solidification dendrites present coarse columnar patterns, with several millimeters in length extending multiple deposition layers. This work not only elucidates the complex interactions among droplet impact dynamics, convective heat transfer, solidification/melting, and wetting phenomena in droplet deposition, but also provides an alternative for the predictions of the DED-Arc additive manufacturing formability, as well as the evolution of convections, temperature, and solidification microstructure.
Keywords:  droplet deposition      DED-Arc additive manufacturing      solidification microstructure      numerical modeling      nickel-based superalloy  
Received:  09 September 2025      Revised:  20 November 2025      Accepted manuscript online:  02 December 2025
PACS:  47.55.Ca (Gas/liquid flows)  
  47.55.D- (Drops and bubbles)  
  91.60.Ed (Crystal structure and defects, microstructure)  
  07.05.Tp (Computer modeling and simulation)  
Fund: Project supported by the National Natural Science Foundation of China (Grant No. 52475389).

Cite this article: 

Qingyu Zhang(张庆宇), Zhixian Chen(陈志贤), Rong Wang(王荣), Pengcheng Huan(环鹏程), Dongke Sun(孙东科), and Xiaonan Wang(王晓南) Multiscale modeling of droplet deposition and solidification dendrite growth during DED-Arc additive manufacturing of a nickel-based superalloy 2026 Chin. Phys. B 35 084701

[1] Xia H X, Yang C and Xu Q Y 2021 Spec. Cast. Nonferrous Alloys 41 1334
[2] Tan C L, Li R S, Su J L, Du D F, Du Y, Attard B, Chew Y X, Zhang H O, Lavernia E J, Fautrelle Y, Teng J and Dong A P 2023 Int. J. Mach. Tools Manuf. 189 104032
[3] Xi N Y, Fang X W, Duan Y S, Zhang Q and Huang K 2022 J. Manuf. Process. 75 1134
[4] Hosseini E and Popovich V A 2019 Addit. Manuf. 30 100877
[5] Zhou J X, Dang L X, Zhang H Q, Yu T T, Mao S C, Duan W, Ji X Y, Shen X, Yin Y J and Li W 2025 Dev. Appl. Mater. 40 1
[6] Huan P C, Wei X, Wang X N, Di H S, Chen Y, Zhang Q Y, Chen X M and Shen X J 2022 Mater. Sci. Eng. A 854 143845
[7] Liu X Y, Di Y L, Wang G, Yuan Q Y and Rong Y M 2025 Addit. Manuf. 98 104649
[8] Brown D W, Losko A, Carpenter J S, Clausen B, Cooley J C, Livescu V, Kenesei P, Park J S, Stockman T J and Strantza M 2020 Metall. Mater. Trans. A 51 1379
[9] Lu W Q, Zhang N F, Ding Z Y, Hu Q D and Li J G 2022 Trans. Nonferrous Met. Soc. China 32 2451
[10] Liu M L, Yi H, Cao H J, Huang R F and Jia L 2021 Addit. Manuf. 48 102413
[11] Liang L J, Hu R Z, Wang J S, Huang A G and Pang S Y 2021 J. Manuf. Process. 69 602
[12] Wang Y Q, Zhou X M, Xiong X C, Yuan Y L, Bai X W, Fu J J and Wu H H 2025 Int. Commun. Heat Mass Transfer 161 108454
[13] Wang L, Ding J L, Zhang X T, Zhang K J, Li H, Ou W M, Peng Y and Wang K H 2025 Int. J. Heat Mass Transfer 238 126455
[14] Cao Y H, Chen C Y, Guo K, Hu T, Xu S Z, Wang J and Ren Z M 2024 Spec. Cast. Nonferrous Alloys 44 1454
[15] Willy H J, Li X W, Tan Y H, Chen Z, Cagirici M, Borayek R, Herng T S, Ong C Y A, Li C J and Ding J 2020 Chin. Phys. B 29 048101
[16] Shi L, Xu S Z, Hou Y Q, Hu T, Wu Y Q, Chen C Y, Wang J and Ren Z M 2025 Metall. Mater. Trans. B 56 5773
[17] Huang J X, Li H Q, Che J Q, Chai Z H, Wang L and Shi B C 2025 Int. J. Heat Mass Transfer 242 126852
[18] Tang S, Li Q, Li W and Chen S 2024 Langmuir 40 18142
[19] Lv Q Y, Lan L L, He B and Wen B H 2025 Phys. Fluids 37 083364
[20] Zhang Y, Zhang S J, Li Y B and Li R 2025 Acta Phys. Sin. 74 108102 (in Chinese)
[21] Tang S F, Wei J J, Yue Y X, Li P Y, Yao M and Wang X D 2025 Acta Metall. Sin. 61 941
[22] Wang Z T, Zhang Q Y, Tan L K and Wang X N 2025 Materials and Solidification 1 9580002
[23] Chen Y, Chen X M, Zhang Q Y, Zhu M F, Liu F, Wang X N, Nagaumi H and Yao Z J 2022 JOM 74 2428
[24] Chen B Y, Zhang Q Y, Sun D K and Wang Z J 2022 J. Cryst. Growth 585 126583
[25] Zhang Q Y, Dong Q P, Wang X N, Wang Z J, Sun D K, Zhu M F, Qian Y H and Nagaumi H 2020 J. Mater. Res. Technol. 9 12080
[26] Li Q, Yu Y and Luo K H 2019 Phys. Rev. E 100 053313
[27] Li Q, Zhou P and Yan H J 2017 Phys. Rev. E 96 063303
[28] Kurz W and Fisher D J 1992 Fundamentals of solidification, 3rd edn. (Switzerland) p. 285
[29] Wang Z T, Chen Z X, Zhang Q Y and Wang X N 2025 J. Cryst. Growth 652 128052
[30] Zhang Q Y, Sun D K, Zhang S H, Wang H and Zhu M F 2020 Chin. Phys. B 29 078104
[31] Yuan P and Schaefer L 2006 Phys. Fluids 18 042101
[32] Zhao Y F, Koizumi Y, Aoyagi K, Wei D X, Yamanaka K and Chiba A 2019 Addit. Manuf. 26 202
[33] Hunziker O, Dye D and Reed R 2000 Acta Mater. 48 4191
[34] Zhang Q Y, Fang H, Xue H, Pan S Y, Rettenmayr M and Zhu M F 2017 Sci. Rep. 7 17809
[35] Solomon A 1966 Math. Comput. 20 347
[36] Huan P C, Wang X N, Zhang Q Y, Di H S, Chen X M, Chen Y and Wei X 2022 J. Mater. Res. Technol. 17 1831
[37] Zhang C X, Qiu Z J, Zhu H L, Wang Z Y, Muransky O, Ionescu M, Pan Z X, Xi J T and Li H J 2021 Metals 12 46
[38] Jang J, Van D and Lee S H 2022 Addit. Manuf. 55 102831
[39] Liu Z Y, Zhao D D, Wang P, Yan M, Yang C, Chen Z W, Lu J and Lu Z P 2022 J. Mater. Sci. Technol. 100 224
[1] Spin and spin-orbit coupling effects in nickel-based superalloys: A first-principles study on Ni3Al doped with Ta/W/Re
Liping Liu(刘立平), Jin Cao(曹晋), Wei Guo(郭伟), and Chongyu Wang(王崇愚). Chin. Phys. B, 2022, 31(1): 016105.
[2] Modeling of microporosity formation and hydrogen concentration evolution during solidification of an Al-Si alloy
Qingyu Zhang(张庆宇), Dongke Sun(孙东科), Shunhu Zhang(章顺虎), Hui Wang(王辉), Mingfang Zhu(朱鸣芳). Chin. Phys. B, 2020, 29(7): 078104.
[3] First-principles study of solute diffusion in Ni3Al
Shaohua Liu(刘少华), Zi Li(李孜), Chongyu Wang(王崇愚). Chin. Phys. B, 2017, 26(9): 093102.
No Suggested Reading articles found!