Stress and strain analysis of Si-based Ⅲ-V template fabricated by ion-slicing

doi:10.1088/1674-1056/ab8a35

Abstract Strain and stress were simulated using finite element method (FEM) for three Ⅲ-V-on-Insulator (Ⅲ-VOI) structures, i.e., InP/SiO₂/Si, InP/Al₂O₃/SiO₂/Si, and GaAs/Al₂O₃/SiO₂/Si, fabricated by ion-slicing as the substrates for optoelectronic devices on Si. The thermal strain/stress imposes no risk for optoelectronic structures grown on InPOI at a normal growth temperature using molecular beam epitaxy. Structures grown on GaAsOI are more dangerous than those on InPOI due to a limited critical thickness. The intermedia Al₂O₃ layer was intended to increase the adherence while it brings in the largest risk. The simulated results reveal thermal stress on Al₂O₃ over 1 GPa, which is much higher than its critical stress for interfacial fracture. InPOI without an Al₂O₃ layer is more suitable as the substrate for optoelectronic integration on Si.

Keywords: Ⅲ-VOI template finite element method (FEM) critical thickness

Received: 03 March 2020
Revised: 26 March 2020
Accepted manuscript online:

PACS:	73.40.Ty	(Semiconductor-insulator-semiconductor structures)
	02.70.Dh	(Finite-element and Galerkin methods)
	62.20.-x	(Mechanical properties of solids)

Fund: Project supported by the National Key Research and Development Program of China (Grant No. 2017YFE0131300)， the National Natural Science Foundation of China (Grant Nos. U1732268, 61874128, 11622545, 61851406, 11705262, and 61804157), the Frontier Science Key Program of the Chinese Academy of Sciences (Grant No. QYZDY-SSW-JSC032), the Chinese-Austrian Cooperative Research and Development Project (Grant No. GJHZ201950), the Science and Technology Innovation Action Plan Program of Shanghai, China (Grant No. 17511106202), the Program of Shanghai Academic Research Leader, China (Grant No. 19XD1404600), the Sailing Program of Shanghai, China (Grant Nos. 19YF1456200 and 19YF1456400), and the K C Wong Education Foundation (Grant No. GJTD-2019-11).

Corresponding Authors: Xin Ou, Shumin Wang
E-mail: ouxin@mail.sim.ac.cn;shumin@chalmers.se

Cite this article:

Shuyan Zhao(赵舒燕), Yuxin Song(宋禹忻), Hao Liang(梁好), Tingting Jin(金婷婷), Jiajie Lin(林家杰), Li Yue(岳丽), Tiangui You(游天桂), Chang Wang(王长), Xin Ou(欧欣), Shumin Wang(王庶民) Stress and strain analysis of Si-based Ⅲ-V template fabricated by ion-slicing 2020 Chin. Phys. B 29 077303

[1]	Schaller R R 1997 IEEE Spectr. 34 52
[2]	Mack C A 2011 IEEE Trans. Semicond. Manuf. 24 202
[3]	Waldrop M M 2016 Nature 530 144
[4]	Krishnamoorthy A V, Ron H, Zheng X, Schwetman H, Lexau J, Koka P, GuoLiang L, Shubin I and Cunningham J E 2009 Proc. IEEE 97 1337
[5]	Lee K K, Lim D R, Kimerling L C, Shin J and Cerrina F 2001 Opt. Lett. 26 1888
[6]	Yao J, Sun Z Z, Zhong L, Natelson D and Tour J M 2010 Nano Lett. 10 4105
[7]	Reed G T, Mashanovich G, Gardes F Y and Thomson D J 2010 Nat. Photon. 4 518
[8]	Michel J, Liu J and Kimerling L C 2010 Nat. Photon. 4 527
[9]	Rong H S, Jones R, Liu A S, Cohen O, Hak D, Fang A and Paniccia M 2005 Nature 433 725
[10]	Wirths S, Geiger R, von den Driesch N, Mussler G, Stoica T, Mantl S, Ikonic Z, Luysberg M, Chiussi S, Hartmann J M, Sigg H, Faist J, Buca D and Grützmacher D 2015 Nat. Photon. 9 88
[11]	Zhou Z P, Yin B and Michel J 2015 Light Sci. Appl. 4 e358
[12]	Liu H Y, Wang T, Jiang Q, Hogg R, Tutu F K, Pozzi F and Seeds A J 2011 Nat. Photon. 5 416
[13]	Lin J J, You T G, Wang M, Huang K, Zhang S B, Jia Q, Zhou M, Yu W J, Zhou S Q, Wang X and Ou X 2018 Nanotechnology 29 504002
[14]	People R and Bean J C 1985 Appl. Phys. Lett. 47 322
[15]	Tadíc M, Peeters F M, Janssens K L, Korkusínski M and Hawrylak P 2002 J. Appl. Phys. 92 5819
[16]	Davies J H 1998 J. Appl. Phys. 84 1358
[17]	Wang S M 2012 Lattice Engineering: Technology and Applications (Singapore: Jenny Stanford Publishing) pp. 63-91
[18]	Huang F Y 2000 Phys. Rev. Lett. 85 784
[19]	Matthews J W and Blakeslee A E 1975 J. Cryst. Growth 29 273
[20]	Lyytinen J, Berdova M, Hirvonen P, Liu X W, Franssila S, Zhou Q and Koskinen J 2014 RSC Adv. 4 37320
[21]	Hibbs-Brenner M K, Morgan R A, Walterson R A, Lehman J A, Kalweit E L, Bounnak S, Marta T and Gieske R 1996 IEEE Photon. Technol. Lett. 8 7
[22]	Tsuchiya T Inoue A and Sakata J 2000 Sens. Actuators 82 286
[23]	Berdova M 2015 Micromechanical characterization of ALD thin films, Ph.D. Dissertation (Helsinki: Aalto University)
[24]	Mercier D, Mandrillon V, Parry G, Verdier M, Estevez R, Bréchet Y and Maindron T 2017 Thin Solid Films 638 34

[1]	Plasmonic characteristics of suspended graphene-coated wedge porous silicon nanowires with Ag partition Xu Wang(王旭), Jue Wang(王珏), Tao Ma(马涛), Heng Liu(刘恒), and Fang Wang(王芳). Chin. Phys. B, 2021, 30(1): 014207.
[2]	Optical modulation of repaired damage site on fused silica produced by CO₂ laser rapid ablation mitigation Chao Tan(谭超), Lin-Jie Zhao(赵林杰), Ming-Jun Chen(陈明君), Jian Cheng(程健), Zhao-Yang Yin(尹朝阳), Qi Liu(刘启), Hao Yang(杨浩), Wei Liao(廖威). Chin. Phys. B, 2020, 29(5): 054209.
[3]	An analytical model of thermal mechanical stress induced by through silicon via Dong Gang (董刚), Shi Tao (石涛), Zhao Ying-Bo (赵颖博), Yang Yin-Tang (杨银堂). Chin. Phys. B, 2015, 24(5): 056601.
[4]	Suppressing the mechanical quadrature error of a quartz double-H gyroscope through laser trimming Zhao Ke (赵克), Feng Li-Hui (冯立辉), Wang Qian-Qian (王茜蒨), Liu Ming-Zhi (刘明智), Wang Ben-Guo (王本国), Cui Fang (崔芳), Sun Yu-Nan (孙雨南). Chin. Phys. B, 2013, 22(11): 117901.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Metrics
Related Articles

Stress and strain analysis of Si-based Ⅲ-V template fabricated by ion-slicing

Cite this article:

Online attention