DETERMINATION OF THE OXYGEN CONTENT IN YBa2Cu3O7-y FILMS

杨秉川1, 王小平1, 石东奇1, 郝建民2, 温业礼2   

  1. (1)General Research Institute for Non-Ferrous Metals, Beijing 100088 , China; (2)Tianjin Electronic Materials Research Institute, Tianjin 300192 , China
  • 收稿日期:1995-01-03 出版日期:1995-10-20 发布日期:1995-10-20

DETERMINATION OF THE OXYGEN CONTENT IN YBa2Cu3O7-y FILMS

HAO JIAN-MIN (郝建民)a, WEN YE-LI (温业礼)a, YANG BING-CHUAN (杨秉川)b, WANG XIAO-PING (王小平)b, SHI DONG-QI (石东奇)b   

  1. a Tianjin Electronic Materials Research Institute, Tianjin 300192 , China; b General Research Institute for Non-Ferrous Metals, Beijing 100088 , China
  • Received:1995-01-03 Online:1995-10-20 Published:1995-10-20

PDF (PC)

348

赞

摘要： A method for determination of the oxygen content (y) in YBa2Cu3O7-y films has been established, in which the lattice conetant difference (b-a) of the films was measured and used to fit the function of (b-a) vs y for the experimental data of bulk YBaaCuaO?-y given in the literature. It is suggested that the function of (b-a) vs y can indeed be used in the case of film. In this process the twin structure of the YBa2Cu3O7-y films was used.

Abstract: A method for determination of the oxygen content (y) in YBa2Cu3O7-y films has been established, in which the lattice conetant difference (b-a) of the films was measured and used to fit the function of (b-a) vs y for the experimental data of bulk YBaaCuaO7-y given in the literature. It is suggested that the function of (b-a) vs y can indeed be used in the case of film. In this process the twin structure of the YBa2Cu3O7-y films was used.