ELECTRICAL RESISTIVITY OF NANOCRYSTALLINE Fe-Cu-Si-B ALLOYS

刘学东, 卢柯, 丁炳哲, 胡壮麒, 王永忠   

  1. State Key Laboratory of Rapidly solidified Nonequilibrium Alloys, Institute of Metal Research, Academia Sinica, Shenyang 110015, China
  • 收稿日期:1993-05-11 出版日期:1994-06-20 发布日期:1994-06-20

ELECTRICAL RESISTIVITY OF NANOCRYSTALLINE Fe-Cu-Si-B ALLOYS

LIU XUE-DONG (刘学东), LU KE (卢柯), DING BING-ZHE (丁炳哲), HU ZHUANG-QI (胡壮麒), WANG YONG-ZHONG (王永忠)   

  1. State Key Laboratory of Rapidly solidified Nonequilibrium Alloys, Institute of Metal Research, Academia Sinica, Shenyang 110015, China
  • Received:1993-05-11 Online:1994-06-20 Published:1994-06-20

PDF (PC)

389

赞

摘要： We have studied the room temperature and low-temperature electrical resistivities of nanocrystalline Fe-Cu-Si-B alloys with various grain sizes prepared by crystallization of amor-phous material. Experimental results showed that with the reduction of grain size both room temperature resistivity ρRT and residual reaistivity ρ0 of the nanostructured alloys studied increased significantly. Based on the scattering effects from interfaces and lattice distortion, the above results were qualitatively discussed.

Abstract: We have studied the room temperature and low-temperature electrical resistivities of nanocrystalline Fe-Cu-Si-B alloys with various grain sizes prepared by crystallization of amor-phous material. Experimental results showed that with the reduction of grain size both room temperature resistivity $\rho$RT and residual reaistivity $\rho$0 of the nanostructured alloys studied increased significantly. Based on the scattering effects from interfaces and lattice distortion, the above results were qualitatively discussed.