Influence of Al3+ doping on the energy levels and thermal property of the 3.5MgO·0.5MgF2·GeO2:Mn4+ red-emitting phosphor

苑琳琳, 张晓松, 徐建萍, 孙健, 金含, 刘晓娟, 李霖霖, 李岚   

  1. Institute of Material Physics, Key Laboratory for Optoelectronic Materials and Devices of Tianjin, Key Laboratory of Display Materials and Photoelectric Devices of Ministry of Education, Tianjin University of Technology, Tianjin 300384, China
  • 收稿日期:2015-01-21 修回日期:2015-03-19 出版日期:2015-08-05 发布日期:2015-08-05
  • 基金资助:
    Project supported by the National High Technology Research and Development Program of China (Grant No. 2013AA014201), the Natural Science Foundation of Tianjin City, China (Grant Nos. 11JCYBJC00300 and 14JCZDJC31200), and the National Key Foundation for Exploring Scientific Instrument of China (Grant No. 2014YQ120351).

Influence of Al3+ doping on the energy levels and thermal property of the 3.5MgO·0.5MgF2·GeO2:Mn4+ red-emitting phosphor

Yuan Lin-lin (苑琳琳), Zhang Xiao-Song (张晓松), Xu Jian-Ping (徐建萍), Sun Jian (孙健), Jin Han (金含), Liu Xiao-Juan (刘晓娟), Li Lin-Lin (李霖霖), Li Lan (李岚)   

  1. Institute of Material Physics, Key Laboratory for Optoelectronic Materials and Devices of Tianjin, Key Laboratory of Display Materials and Photoelectric Devices of Ministry of Education, Tianjin University of Technology, Tianjin 300384, China
  • Received:2015-01-21 Revised:2015-03-19 Online:2015-08-05 Published:2015-08-05
  • Contact: Li Lan E-mail:lilan@tjut.edu.cn
  • Supported by:
    Project supported by the National High Technology Research and Development Program of China (Grant No. 2013AA014201), the Natural Science Foundation of Tianjin City, China (Grant Nos. 11JCYBJC00300 and 14JCZDJC31200), and the National Key Foundation for Exploring Scientific Instrument of China (Grant No. 2014YQ120351).

RichHTML

0

PDF (PC)

690

赞

摘要： A series of Al3+-doped 3.5MgO·0.5MgF2·GeO2:Mn4+ red-emitting phosphors is synthesized by high temperature solid-state reaction. The broad excitation band at 300 nm-380 nm, resulting from the 4A2 → 4T1 transition of Mn4+, exhibits a blue shift with the increase of Al2O3 content. The observation of the decreased Mn4+-O2- distance is explained by the crystal field theory. The temperature-dependent photoluminescence spectra with various amounts of Al2O3 content are comparatively measured and the calculation shows that the activation energy increases up to 0.41 eV at the Al2O3 content of 0.1 mol. The maximum phonon densities of state for these samples are calculated from Raman spectra and they are correlated with the thermal properties.

关键词: phosphors, photoluminescence, thermal properties

Abstract: A series of Al3+-doped 3.5MgO·0.5MgF2·GeO2:Mn4+ red-emitting phosphors is synthesized by high temperature solid-state reaction. The broad excitation band at 300 nm-380 nm, resulting from the 4A2 → 4T1 transition of Mn4+, exhibits a blue shift with the increase of Al2O3 content. The observation of the decreased Mn4+-O2- distance is explained by the crystal field theory. The temperature-dependent photoluminescence spectra with various amounts of Al2O3 content are comparatively measured and the calculation shows that the activation energy increases up to 0.41 eV at the Al2O3 content of 0.1 mol. The maximum phonon densities of state for these samples are calculated from Raman spectra and they are correlated with the thermal properties.

Key words: phosphors, photoluminescence, thermal properties