Double-layer microwave absorber of nanocrystalline strontium ferrite and iron microfibers

doi:10.1088/1674-1056/21/2/028101

中国物理B ›› 2012, Vol. 21 ›› Issue (2): 28101-028101.doi: 10.1088/1674-1056/21/2/028101

韦春余,沈湘黔,宋福展

收稿日期:2011-08-17 修回日期:2011-09-16 出版日期:2012-01-30 发布日期:2012-01-30
通讯作者: 沈湘黔,shenxq@ujs.edu.cn E-mail:shenxq@ujs.edu.cn

Double-layer microwave absorber of nanocrystalline strontium ferrite and iron microfibers

Wei Chun-Yu(韦春余), Shen Xiang-Qian(沈湘黔)^†, and Song Fu-Zhan(宋福展)

School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, China

Received:2011-08-17 Revised:2011-09-16 Online:2012-01-30 Published:2012-01-30
Contact: Shen Xiang-Qian,shenxq@ujs.edu.cn E-mail:shenxq@ujs.edu.cn
Supported by:
Project supported by the Aviation Science Foundation, China (Grant No. 2009ZF52063), the Research Fund for the Doctoral Program of Higher Education of China (Grant No. 20103227110006), and the Jiangsu Provincial Postgraduate Cultivation and Innovation Project, China (Grant No. CX10B-257Z).

摘要/Abstract

Abstract: Microwave absorption properties of the nanocrystalline strontium ferrite (SrFe₁₂O₁₉) and iron ($\alpha$-Fe) microfibers for single-layer and double-layer structures are investigated in a frequency range of 2 GHz-18 GHz. For the single-layer absorbers, the nanocrystalline SrFe₁₂O₁₉ microfibers show some microwave absorptions at 6 GHz-18 GHz, with a minimum reflection loss (RL) value of -11.9 dB at 14.1 GHz for a specimen thickness of 3.0 mm, while for the nanocrystalline $\alpha$-Fe microfibers, their absorptions largely take place at 15 GHz-18 GHz with the RL value exceeding -10 dB, with a minimum RL value of about -24 dB at 17.5 GHz for a specimen thickness of 0.7 mm. For the double-layer absorber with an absorbing layer of α-Fe microfibers with a thickness of 0.7 mm and matching layer of SrFe₁₂O₁₉ microfibers with a thickness of 1.3 mm, the minimum RL value is about -63 dB at 16.4 GHz and the absorption band width is about 6.7 GHz ranging from 11.3 GHz to 18 GHz with the RL value exceeding -10 dB which covers the whole K_u-band (12.4 GHz-18 GHz) and 27% of X-band (8.2 GHz-12.4 GHz).

Key words: nanocrystalline microfibers, microwave absorber, double-layer structure

中图分类号: (Nanocrystalline materials)

81.07.Bc

75.50.-y (Studies of specific magnetic materials) 73.21.Ac (Multilayers)

韦春余, 沈湘黔, 宋福展. [J]. 中国物理B, 2012, 21(2): 28101-028101.

Wei Chun-Yu(韦春余), Shen Xiang-Qian(沈湘黔), and Song Fu-Zhan(宋福展) . Double-layer microwave absorber of nanocrystalline strontium ferrite and iron microfibers[J]. Chin. Phys. B, 2012, 21(2): 28101-028101.

参考文献 30

[1]	Yang Y L, Gupta M C, Dudley K L and Lawrence R W 2005 Nano Lett. 5 2131
[2]	Han M G, Ou Y, Liang D F and Deng L J 2009 Chin. Phys. B 18 1261
[3]	Liu X G, Geng D Y, Meng H, Li B, Zhang Q, Kang D J and Zhang Z D E 2008 J. Phys. D: Appl. Phys. 41 175001
[4]	Oikonomou A, Giannakopoulou T and Litsardakis G 2007 J. Magn. Magn. Mater. 316 e827
[5]	Lu H P, Han M G, Cai L and Deng L J 2011 Chin. Phys. B 20 060701
[6]	Sun G B, Dong B X, Cao M H, Wei B Q and Hu C H 2011 Chem. Mater. 23 1587
[7]	Duan Y P, Yang Y, He M, Liu S H, Cui X D and Chen H F 2008 J. Phys. D: Appl. Phys. 41 125403
[8]	Zhang X Z and Sun W 2010 Cement Concrete Compd. 32 726
[9]	Chen L Y, Duan Y P, Liu L D, Guo J B and Liu S H 2011 Mater. Design 32 570
[10]	Qing Y C, Zhou W C, Luo F and Zhu D M 2011 J. Magn. Magn. Mater. 323 600
[11]	S黵ig C, Hempel K A and Bonnenberg D 1993 Appl. Phys. Lett. 63 2836
[12]	Chen N, Mu G H, Pan X F, Gan K K and Gu M Y 2007 Mater. Sci. Eng. B 139 256
[13]	Cho H S and Kim S S 1999 IEEE Trans. Magn. 35 3151
[14]	Ghasemi A, Hossienpour A Morisako A, Saatchi A and Salehi M 2006 J. Magn. Magn. Mater. 302 429
[15]	Liu J R, Itoh M and Machida K 2003 Chem. Lett. 32 394
[16]	Zhang X F, Dong X L, Huang H, Liu Y Y, Wang W N, Zhu X G, L? B and Lei J P 2006 Appl. Phys. Lett. 89 053115
[17]	Zhang X F, Dong X L, Huang H, Liu Y Y, L? B, Lei J P and Choi C J 2007 J. Phys. D: Appl. Phys. 40 5383
[18]	Liu J R, Itoh M, Terada M, Horikawa T and Machida K 2007 Appl. Phys. Lett. 91 093101
[19]	Rousselle D, Berthault A, Acher O, Bouchaud J P and Zerah P G 1993 J. Appl. Phys. 74 475
[20]	Song F Z, Shen X Q, Liu M Q and Xiang 2011 J. Mater. Chem. Phys. 126 791
[21]	Shen X Q, Jing M X, Wang T P and Cao K 2006 Rare Metal Mat. Eng. 35 945 (in Chinese)
[22]	Aharoni A 1996 J. Appl. Phys. 81 830
[23]	Michielssen Y, Sager J M, Ranjithan S and Mittra R 1993 Microw. Theory Tech. 41 1024
[24]	Neelakanta P S 1990 J. Phys.: Condens. Matter 2 4935
[25]	Ramo S Whinnery J R and Duzer T V 1984 Fields and Waves in Communication Electronics (New York: Wiley) p. 36
[26]	Mercier D, L関y J C S, Viau G, Fi関et-Vincent F, Fi関et F, Toneguzzo P and Acher O 2000 Phys. Rev. B 62 532
[27]	Watts P C P, Hsu W K, Barnes A and Chambers B 2003 Adv. Mater. 15 600
[28]	Snoek J L 1948 Physica (Amsterdam) 14 207
[29]	Pullar R C, Appleton S G and Bhattacharya A K 1998 J. Magn. Magn. Mater. 186 326
[30]	Guo W K, Li J J, Zhao N Q and Zhou F G 2003 Aerosp. Mater. Technol. 33 12

Double-layer microwave absorber of nanocrystalline strontium ferrite and iron microfibers

PDF (PC)

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献 30

相关文章 15

Metrics

本文评价

推荐阅读 0

[1]	Ni Suo(索妮), Longsheng Cao(曹龙生), Xiaoping Qin(秦晓平), and Zhigang Shao(邵志刚). Research progress of Pt and Pt-based cathode electrocatalysts for proton-exchange membrane fuel cells[J]. 中国物理B, 2022, 31(12): 128108-128108.
[2]	Zein K. Heiba, Mohamed Bakr Mohamed, Ali A. Alkathiri, Sameh I. Ahmed, A A Alhazime. Impact of composition ratio on the structure and optical properties of (1-x)MnFe₂O₄/(x)ZnMn₂O₄ nanocomposite[J]. 中国物理B, 2022, 31(7): 77102-077102.
[3]	. [J]. 中国物理B, 2021, 30(3): 38103-.
[4]	常爱玲, 毛亦琛, 黄志伟, 洪海洋, 徐剑芳, 黄巍, 陈松岩, 李成. Low-temperature plasma enhanced atomic layer deposition of large area HfS₂ nanocrystal thin films[J]. 中国物理B, 2020, 29(3): 38102-038102.
[5]	卢晨曦, 余森江, 李领伟, 杨波, 陶向明, 叶高翔. A low-dimensional crystal growth model on an isotropic and quasi-free sustained substrate[J]. 中国物理B, 2020, 29(3): 38101-038101.
[6]	钱凯, 高蕾, 李航, 张帅, 严佳浩, 刘晨, 王嘉鸥, 钱天, 丁洪, 张余洋, 林晓, 杜世萱, 高鸿钧. Epitaxial growth and air-stability of monolayer Cu₂Te[J]. 中国物理B, 2020, 29(1): 18104-018104.
[7]	闫文君, 曾小敏, 刘欢, 郭春伟, 凌敏, 周后盘. Highly reliable and selective ethanol sensor based on α-Fe₂O₃ nanorhombs working in realistic environments[J]. 中国物理B, 2019, 28(10): 106801-106801.
[8]	J Mohammed, A B Suleiman, Tchouank Tekou Carol T, H Y Hafeez, Jyoti Sharma, Pradip K Maji, Sachin Godara Kumar, A K Srivastava. Enhanced dielectric and optical properties of nanoscale barium hexaferrites for optoelectronics and high frequency application[J]. 中国物理B, 2018, 27(12): 128104-128104.
[9]	赵宣, 何大伟, 王永生, 付晨. In situ growth of different numbers of gold nanoparticles on MoS₂ with enhanced electrocatalytic activity for hydrogen evolution reaction[J]. 中国物理B, 2018, 27(6): 68103-068103.
[10]	许贺菊, 米建松, 李云, 张彬, 丛日东, 傅广生, 于威. Nucleation mechanism and morphology evolution of MoS₂ flakes grown by chemical vapor deposition[J]. 中国物理B, 2017, 26(12): 128102-128102.
[11]	Abdolvahab Amirsalari,Saber Farjami Shayesteh,Reza Taheri Ghahrizjani. Intrinsic luminescence centers in γ- and θ-alumina nanoparticles[J]. 中国物理B, 2017, 26(3): 36101-036101.
[12]	E Mehran, S Farjami Shayesteh, M Sheykhan. Structural and magnetic properties of turmeric functionalized CoFe₂O₄ nanocomposite powder[J]. 中国物理B, 2016, 25(10): 107504-107504.
[13]	屠林林, 张弛, 黄忠, 詹鹏, Jason Yau, 王振林. A high-quality factor hybrid plasmonic nanocavity based on distributed Bragg reflectors[J]. 中国物理B, 2016, 25(9): 97302-097302.
[14]	王勐, 周旸, 段军飞, 谌东中. Azobenzene mesogens mediated preparation of SnS nanocrystals encapsulated with in-situ N-doped carbon and their enhanced electrochemical performance for lithium ion batteries application[J]. 中国物理B, 2016, 25(9): 96102-096102.
[15]	乔泊, 赵谡玲, 徐征, 徐叙瑢. Synthesis of ZnO quantum dots and their agglomeration mechanisms along with emission spectra based on ageing time and temperature[J]. 中国物理B, 2016, 25(9): 98102-098102.