Improved electrochemical performances of high voltage LiCoO2 with tungsten doping

Jie-Nan Zhang(张杰男), Qing-Hao Li(李庆浩), Quan Li(李泉), Xi-Qian Yu(禹习谦), Hong Li(李泓)   

  1. 1 Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China;
    2 School of Physical Sciences, University of Chinese Academy of Sciences, Beijing 100190, China
  • 收稿日期:2018-04-08 修回日期:2018-05-23 出版日期:2018-08-05 发布日期:2018-08-05
  • 通讯作者: Xi-Qian Yu, Hong Li E-mail:xyu@iphy.ac.cn;hli@iphy.ac.cn

Improved electrochemical performances of high voltage LiCoO2 with tungsten doping

Jie-Nan Zhang(张杰男)1,2, Qing-Hao Li(李庆浩)1, Quan Li(李泉)1,2, Xi-Qian Yu(禹习谦)1, Hong Li(李泓)1,2   

  1. 1 Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China;
    2 School of Physical Sciences, University of Chinese Academy of Sciences, Beijing 100190, China
  • Received:2018-04-08 Revised:2018-05-23 Online:2018-08-05 Published:2018-08-05
  • Contact: Xi-Qian Yu, Hong Li E-mail:xyu@iphy.ac.cn;hli@iphy.ac.cn

摘要:

The effects of tungsten W doping and coating on the electrochemical performance of LiCoO2 cathode are comparatively studied in this work. The amount of modification component is as low as 0.1 wt% and 0.3 wt% respectively. After 100 cycles between 3.0 V-4.6 V, 0.1 wt% W doping provides an optimized capacity retention of 72.3%. However, W coating deteriorates battery performance with capacity retention of 47.8%, even lower than bare LiCoO2 of 55.7%. These different electrochemical performances can be attributed to the surface aggregation of W between doping and coating methods. W substitution is proved to be a promising method to develop high voltage cathodes. Practical performance relies on detailed synthesis method.

关键词: cathode, lithium-ion batteries, lithium cobalt oxide, doping, coating

Abstract:

The effects of tungsten W doping and coating on the electrochemical performance of LiCoO2 cathode are comparatively studied in this work. The amount of modification component is as low as 0.1 wt% and 0.3 wt% respectively. After 100 cycles between 3.0 V-4.6 V, 0.1 wt% W doping provides an optimized capacity retention of 72.3%. However, W coating deteriorates battery performance with capacity retention of 47.8%, even lower than bare LiCoO2 of 55.7%. These different electrochemical performances can be attributed to the surface aggregation of W between doping and coating methods. W substitution is proved to be a promising method to develop high voltage cathodes. Practical performance relies on detailed synthesis method.

Key words: cathode, lithium-ion batteries, lithium cobalt oxide, doping, coating