Effect of microstructure on 3He migration in TiT1.9 films

Haifeng Wang(王海峰), Shuming Peng(彭述明), Wei Ding(丁伟), Huahai Shen(申华海), Weidu Wang(王维笃), Xiaosong Zhou(周晓松), Xinggui Long(龙兴贵)   

  1. Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621900, China
  • 收稿日期:2018-03-11 修回日期:2018-05-27 出版日期:2018-09-05 发布日期:2018-09-05
  • 通讯作者: Shuming Peng E-mail:pengshuming@caep.cn

Effect of microstructure on 3He migration in TiT1.9 films

Haifeng Wang(王海峰), Shuming Peng(彭述明), Wei Ding(丁伟), Huahai Shen(申华海), Weidu Wang(王维笃), Xiaosong Zhou(周晓松), Xinggui Long(龙兴贵)   

  1. Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621900, China
  • Received:2018-03-11 Revised:2018-05-27 Online:2018-09-05 Published:2018-09-05
  • Contact: Shuming Peng E-mail:pengshuming@caep.cn

摘要:

Two kinds of films were prepared to study the effect of microstructure on helium migration in Ti tritides. Both films showed different release behaviors and helium bubble distributions. In the film consisting of columnar grains, a two-layered structure was observed. Inclusions with a strip feature were found at the grain boundary, and no helium bubbles were distributed in these inclusions. However, helium preferred to migrate to the boundaries of these inclusions. Bubble linkage as a ribbon-like feature developed parallel to the film surface in the film consisting of columnar grains. More cracks were developed at the grain boundaries of the film consisting of columnar grains, although the helium content in the film consisting of columnar grains was less than that in the film consisting of equiaxed grains. A surface region with a small number of bubbles, or “depleted zone”, was observed near the surface. The cracks extending to the film surface were the pathways of the critical helium released from the film. The helium migration was strongly influenced by the grain microstructure.

关键词: helium bubble, Ti tritide, microstructure

Abstract:

Two kinds of films were prepared to study the effect of microstructure on helium migration in Ti tritides. Both films showed different release behaviors and helium bubble distributions. In the film consisting of columnar grains, a two-layered structure was observed. Inclusions with a strip feature were found at the grain boundary, and no helium bubbles were distributed in these inclusions. However, helium preferred to migrate to the boundaries of these inclusions. Bubble linkage as a ribbon-like feature developed parallel to the film surface in the film consisting of columnar grains. More cracks were developed at the grain boundaries of the film consisting of columnar grains, although the helium content in the film consisting of columnar grains was less than that in the film consisting of equiaxed grains. A surface region with a small number of bubbles, or “depleted zone”, was observed near the surface. The cracks extending to the film surface were the pathways of the critical helium released from the film. The helium migration was strongly influenced by the grain microstructure.

Key words: helium bubble, Ti tritide, microstructure