1373K isothermal section of phase diagram for Nb-W-Zr ternary system

夏长清1, 李炜2   

  1. (1)School of Material Science and Engineering, Central South University, Changsha410083,P.R.China; (2)School of Physics and Telecommunication Engineering, South China Normal University, Guangzhou510631, China
  • 收稿日期:2004-11-03 修回日期:2005-01-24 出版日期:2005-05-19 发布日期:2005-05-19
  • 基金资助:
    Project supported by the National Natural Foundation of China ( Grant No.59871066).

1373K isothermal section of phase diagram for Nb-W-Zr ternary system

Li Wei (李炜)a, Xia Chang-Qing (夏长清)b    

  1. a School of Physics and Telecommunication Engineering, South China Normal University, Guangzhou 510631, China; b School of Material Science and Engineering, Central South University, Changsha 410083, China
  • Received:2004-11-03 Revised:2005-01-24 Online:2005-05-19 Published:2005-05-19
  • Supported by:
    Project supported by the National Natural Foundation of China ( Grant No.59871066).

PDF (PC)

605

赞

摘要： The isothermal section of the Nb-W-Zr system at 1373K has been successfully measured by means of electron probe microanalysis(EPMA) on diffusion couples. This isothermal section includes two single-phase regions, "α" and (W,Nb)2Zr, and one two-phase region "α" + (W,Nb)2Zr. The maximum solid solubility of Nb in (W,Nb)2Zr is 12.23at.% Nb.

关键词: diffusion-couple, phase diagram, Nb-W-Zr

Abstract: The isothermal section of the Nb-W-Zr system at 1373K has been successfully measured by means of electron probe microanalysis(EPMA) on diffusion couples. This isothermal section includes two single-phase regions, "$\alpha$" and (W,Nb)2Zr, and one two-phase region "$\alpha$" + (W,Nb)2Zr. The maximum solid solubility of Nb in (W,Nb)2Zr is 12.23at.% Nb.