中国物理B ›› 2004, Vol. 13 ›› Issue (11): 1918-1921.doi: 10.1088/1009-1963/13/11/027

• • 上一篇    下一篇

Electrical conductivity of individual polypyrrole microtube

龙云泽1, 陈兆甲1, 金爱子2, 顾长志2, 万梅香3, 肖红梅4   

  1. (1)Key Laboratory of Extreme Conditions Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100080, China; (2)Laboratory of Microfabrication, Institute of Physics, Chinese Academy of Sciences, Beijing 100080, China; (3)Laboratory of Organic Solids, Centre for Molecular Sciences, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100080, China; (4)Laboratory of Organic Solids, Centre for Molecular Sciences, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100080, China; School of Chemical and Environmental Engineering, China University of Mining and Technology (Beijing), Beijing 100083, China
  • 收稿日期:2004-02-13 修回日期:2003-04-08 出版日期:2004-11-20 发布日期:2005-06-20
  • 基金资助:
    Project supported by the National Natural Science Foundation of China (Grant No 10374107).

Electrical conductivity of individual polypyrrole microtube

Long Yun-Ze (龙云泽)a,  Xiao Hong-Mei (肖红梅)bc, Chen Zhao-Jia (陈兆甲)a, Wan Mei-Xiang (万梅香)b, Jin Ai-Zi (金爱子)d, Gu Chang-Zhi (顾长志)d    

  1. a Key Laboratory of Extreme Conditions Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100080, China; b Laboratory of Organic Solids, Centre for Molecular Sciences, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100080, China; c School of Chemical and Environmental Engineering, China University of Mining and Technology (Beijing), Beijing 100083, China; d Laboratory of Microfabrication, Institute of Physics, Chinese Academy of Sciences, Beijing 100080, China
  • Received:2004-02-13 Revised:2003-04-08 Online:2004-11-20 Published:2005-06-20
  • Supported by:
    Project supported by the National Natural Science Foundation of China (Grant No 10374107).

PDF (PC)

574

赞

摘要： Conducting microtubes (0.4－0.5μm in outer diameter) made of polypyrrole (PPy) doped with p-toluene sulfonic acid (PTSA) were synthesized by a self-assembly method. We report the electrical conductivity of an individual PPy microtube, on which a pair of platinum micro-leads was fabricated by focused ion beam deposition. The measured room-temperature conductivity of the individual PPy microtube was 0.29S/cm, which is comparable to that of template-synthesized PPy micro/nanotubes. The temperature dependence of conductivity of the individual microtube follows the three-dimensional variable-range hopping (3D VRH) model.

关键词: conducting polymers, microtubes, self-assembly, conductivity, polypyrrole

Abstract: Conducting microtubes (0.4－0.5μm in outer diameter) made of polypyrrole (PPy) doped with p-toluene sulfonic acid (PTSA) were synthesized by a self-assembly method. We report the electrical conductivity of an individual PPy microtube, on which a pair of platinum micro-leads was fabricated by focused ion beam deposition. The measured room-temperature conductivity of the individual PPy microtube was 0.29S/cm, which is comparable to that of template-synthesized PPy micro/nanotubes. The temperature dependence of conductivity of the individual microtube follows the three-dimensional variable-range hopping (3D VRH) model.

Key words: conducting polymers, microtubes, self-assembly, conductivity, polypyrrole

中图分类号:  (Polymers; organic compounds (including organic semiconductors))

  • 72.80.Le
61.46.-w (Structure of nanoscale materials)