Synthesis and photoluminescence properties of Nd2O3 nanoparticles modified by sodium bis 2-ethylhexyl sulfosuccinate

任建华1, 赵同刚1, 刘建华2, 孔娟2, 贺加欣2, 郭林2   

  1. (1)School of Electronic Engineering, Beijing University of Posts and Telecommunication, Beijing 100876, China; (2)School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China
  • 收稿日期:2007-12-21 修回日期:2008-04-16 出版日期:2008-12-20 发布日期:2008-12-20
  • 基金资助:
    Project supported by State Key Project of Fundamental Research for Nanoscience and Nanotechnology (Grant No 2006CB932300) and the National Natural Science Foundation of China (Grant No 50725208).

Synthesis and photoluminescence properties of Nd2O3 nanoparticles modified by sodium bis(2-ethylhexyl) sulfosuccinate

Ren Jian-Hua (任建华)a, Zhao Tong-Gang (赵同刚)a, Liu Jian-Hua (刘建华)b, Kong Juan (孔娟)b, He Jia-Xin (贺加欣)b, Guo Lin (郭林)b   

  1. a School of Electronic Engineering, Beijing University of Posts and Telecommunication, Beijing 100876, China; b School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China
  • Received:2007-12-21 Revised:2008-04-16 Online:2008-12-20 Published:2008-12-20
  • Supported by:
    Project supported by State Key Project of Fundamental Research for Nanoscience and Nanotechnology (Grant No 2006CB932300) and the National Natural Science Foundation of China (Grant No 50725208).

PDF (PC)

636

赞

摘要： This paper reports that Nd2O3 nanoparticles modified by AOT(sodium bis(2-ethylhexyl) sulfosuccinate) were prepared using microemulsion method in the system of water and propanol/AOT/toluene. Transmission electron microscopy shows that the Nd2O3 nanoparticles take the shape of sphere with 18\,nm and 31nm with different preparation. The organic sol of Nd2O3 nanoparticles is very stable at room temperature. X-ray diffraction results show that the product has hexagonal phase structure. Two ultraviolet emission band at 344\,nm and 361\,nm corresponding to the transition of 4D3/2→4I9/2 and 2P3/2→4I112 or 4D3/2 →4I13/2 were observed.

关键词: Nd2O3 nanocrystals, photoluminescence spectrum, surface modification

Abstract: This paper reports that Nd2O3 nanoparticles modified by AOT(sodium bis(2-ethylhexyl) sulfosuccinate) were prepared using microemulsion method in the system of water and propanol/AOT/toluene. Transmission electron microscopy shows that the Nd2O3 nanoparticles take the shape of sphere with 18 nm and 31nm with different preparation. The organic sol of Nd2O3 nanoparticles is very stable at room temperature. X-ray diffraction results show that the product has hexagonal phase structure. Two ultraviolet emission band at 344 nm and 361\,nm corresponding to the transition of 4D3/2→4I9/2 and 2P3/2→4I112 or 4D3/2 →4I13/2 were observed.

Key words: Nd2O3 nanocrystals, photoluminescence spectrum, surface modification

中图分类号:  (Methods of micro- and nanofabrication and processing)

  • 81.16.-c
61.46.Df (Structure of nanocrystals and nanoparticles ("colloidal" quantum dots but not gate-isolated embedded quantum dots)) 68.37.Lp (Transmission electron microscopy (TEM)) 78.55.Hx (Other solid inorganic materials) 78.67.Bf (Nanocrystals, nanoparticles, and nanoclusters) 81.07.Bc (Nanocrystalline materials)