Heat treatment on phase evolution of Bi-2223 precursor powder prepared by spray pyrolysis method

Li-Jun Cui(崔利军), Ping-Xiang Zhang(张平祥), Jin-Shan Li(李金山), Guo Yan(闫果), Yong Feng(冯勇), Xiang-Hong Liu(刘向宏), Jian-Feng Li(李建峰), Xi-Feng Pan(潘熙峰), Fan Yang(杨帆), Sheng-Nan Zhang(张胜楠), Xiao-Bo Ma(马晓波), Guo-Qing Liu(刘国庆)   

  1. 1 State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China;
    2 National Engineering Laboratory for Superconducting Materials(NELSM), Western Superconducting Technologies(WST) Co. Ltd., Xi'an 710018, China;
    3 Superconducting Materials Center, Northwest Institute for Nonferrous Metal Research, Xi'an 710016, China
  • 收稿日期:2018-09-27 修回日期:2019-01-27 出版日期:2019-04-05 发布日期:2019-04-05
  • 通讯作者: Ping-Xiang Zhang E-mail:cljwst@163.com
  • 基金资助:

    Project supported by the National Key Research and Development Program of China (Grant No. 2017YFB0902303), the Key Research and Development Program of Shaanxi Province, China (Grant No. 2018GY-121N), and the National Key Project of Magneto Constrained Fusion Energy Development Program, China (Grant No. 2015GB115001).

Heat treatment on phase evolution of Bi-2223 precursor powder prepared by spray pyrolysis method

Li-Jun Cui(崔利军)1,2, Ping-Xiang Zhang(张平祥)1,2,3, Jin-Shan Li(李金山)1, Guo Yan(闫果)2, Yong Feng(冯勇)2, Xiang-Hong Liu(刘向宏)2, Jian-Feng Li(李建峰)2, Xi-Feng Pan(潘熙峰)2, Fan Yang(杨帆)2, Sheng-Nan Zhang(张胜楠)3, Xiao-Bo Ma(马晓波)3, Guo-Qing Liu(刘国庆)3   

  1. 1 State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China;
    2 National Engineering Laboratory for Superconducting Materials(NELSM), Western Superconducting Technologies(WST) Co. Ltd., Xi'an 710018, China;
    3 Superconducting Materials Center, Northwest Institute for Nonferrous Metal Research, Xi'an 710016, China
  • Received:2018-09-27 Revised:2019-01-27 Online:2019-04-05 Published:2019-04-05
  • Contact: Ping-Xiang Zhang E-mail:cljwst@163.com
  • Supported by:

    Project supported by the National Key Research and Development Program of China (Grant No. 2017YFB0902303), the Key Research and Development Program of Shaanxi Province, China (Grant No. 2018GY-121N), and the National Key Project of Magneto Constrained Fusion Energy Development Program, China (Grant No. 2015GB115001).

摘要:

The phase evolution of Bi-2223 precursor powder prepared by spray pyrolysis method is studied with different heat treatment parameters. The results show that the reaction temperature and phase composition of precursor powder depend on heat treatment atmosphere. Phase assemblage of (Bi,Pb)-2212, AEC, CuO, and small Bi-2201 can be obtained by heat-treated in N2-0.1%O2 atmosphere. For precursor powder, there is sufficient reaction process at 770℃, and the dimension of Bi-2212 phase increases rapidly with the increase of heat treatment temperature and time. The dimension of AEC phase also increases by extending heat treatment time. As a balance among phase assemblage, dimension of particle and adequate reaction, a reasonable precursor powder can be obtained by heat-treated at 770℃ for 12 h-16 h in N2-0.1%O2 atmosphere. Critical current of 37-filament Bi-2223 tape is about 120 A, which confirms that these heat treatment parameters are reasonable.

关键词: Bi-2223, phase evolution, heat treatment, spray pyrolysis

Abstract:

The phase evolution of Bi-2223 precursor powder prepared by spray pyrolysis method is studied with different heat treatment parameters. The results show that the reaction temperature and phase composition of precursor powder depend on heat treatment atmosphere. Phase assemblage of (Bi,Pb)-2212, AEC, CuO, and small Bi-2201 can be obtained by heat-treated in N2-0.1%O2 atmosphere. For precursor powder, there is sufficient reaction process at 770℃, and the dimension of Bi-2212 phase increases rapidly with the increase of heat treatment temperature and time. The dimension of AEC phase also increases by extending heat treatment time. As a balance among phase assemblage, dimension of particle and adequate reaction, a reasonable precursor powder can be obtained by heat-treated at 770℃ for 12 h-16 h in N2-0.1%O2 atmosphere. Critical current of 37-filament Bi-2223 tape is about 120 A, which confirms that these heat treatment parameters are reasonable.

Key words: Bi-2223, phase evolution, heat treatment, spray pyrolysis