Synthesis of hexagonal monocrystal AlN microtubes and nanowires at low temperature

陈光德1, 颜国君1, 耶红刚1, 吕惠民2   

  1. (1)Department of Applied Physics, Xi'an Jiaotong University, Xi'an 710049, China; (2)Department of Applied Physics, Xi'an Jiaotong University, Xi'an 710049, China;Department of Applied Physics, Xi'an University of Technology, Xi'an 710048, China
  • 收稿日期:2006-11-23 修回日期:2007-01-29 出版日期:2007-09-20 发布日期:2007-09-20
  • 基金资助:
    Project supported by the National Natural Science Foundation of China (Grant No 10474078) and the Science Foundation of the Education Office of Shanxi Province, China.

Synthesis of hexagonal monocrystal AlN microtubes and nanowires at low temperature

Lv Hui-Min(吕惠民)a)b), Chen Guang-De(陈光德)a), Yan Guo-Jun(颜国君)a, and Ye Hong-Gang(耶红刚)a)   

  1. a Department of Applied Physics, Xi'an Jiaotong University, Xi'an 710049, China; b Department of Applied Physics, Xi'an University of Technology, Xi'an 710048, China
  • Received:2006-11-23 Revised:2007-01-29 Online:2007-09-20 Published:2007-09-20
  • Supported by:
    Project supported by the National Natural Science Foundation of China (Grant No 10474078) and the Science Foundation of the Education Office of Shanxi Province, China.

PDF (PC)

523

赞

摘要： This paper reports that pure hexagonal aluminium nitride microtubes and nanowires growing along the [0001] direction have been successfully synthesized by directly reacting AlCl$_{3}$ with NaN$_{3}$ at low temperature (450\du) under condition of non-solvent system. The grey--white powder of reacting product was characterized by high-resolution transmission electron microscope (HRTEM), which shows that the powder is long straight-wire morphology with outer diameter from 40\,nm to 300\,nm and length up to several micrometres. The results of both electron diffraction (ED) and x-ray diffraction (XRD) indicate that the AlN microtubes have a pure hexagonal monocrystal tubular structure with the combination of the curled AlN nanobelts. Room-temperature photoluminescence spectrum of the synthesized sample showed an emission peak, which is closely related to the small size of the microtubes.

关键词: h-AlN, microtubes, nanowires

Abstract: This paper reports that pure hexagonal aluminium nitride microtubes and nanowires growing along the [0001] direction have been successfully synthesized by directly reacting AlCl$_{3}$ with NaN$_{3}$ at low temperature (450℃) under condition of non-solvent system. The grey--white powder of reacting product was characterized by high-resolution transmission electron microscope (HRTEM), which shows that the powder is long straight-wire morphology with outer diameter from 40 nm to 300 nm and length up to several micrometres. The results of both electron diffraction (ED) and x-ray diffraction (XRD) indicate that the AlN microtubes have a pure hexagonal monocrystal tubular structure with the combination of the curled AlN nanobelts. Room-temperature photoluminescence spectrum of the synthesized sample showed an emission peak, which is closely related to the small size of the microtubes.

Key words: h-AlN, microtubes, nanowires

中图分类号:  (Methods of materials synthesis and materials processing)