Nanocrystal formation and structure in oxyfluoride glass ceramics

余华, 赵丽娟, 孟婕, 梁沁, 禹宣伊, 唐柏权, 许京军   

  1. Photonics Research Center, College of Physical Science, Nankai University,Tianjin 300071, China;The MOE Key Laboratory of Advanced Technique & Fabrication for Weak-Light Nonlinear Photonics Materials,and Tianjin Key Laboratory of Photonics Materials & Tec
  • 收稿日期:2005-11-25 修回日期:2005-06-02 出版日期:2005-09-20 发布日期:2005-09-20
  • 基金资助:
    Project supported by the National Natural Scientific foundation of China (Grant No 60178024) and the Cultivation Fund of the Key Scientific and Technical Innovation Project,Ministry of Education of China (Grant No 704012).

Nanocrystal formation and structure in oxyfluoride glass ceramics

Yu Hua (余华), Zhao Li-Juan (赵丽娟), Meng Jie (孟婕), Liang Qin (梁沁), Yu Xuan-Yi (禹宣伊), Tang Bai-Quan (唐柏权), Xu Jing-Jun (许京军)   

  1. Photonics Research Center, College of Physical Science, Nankai University,Tianjin 300071, China; The MOE Key Laboratory of Advanced Technique & Fabrication for Weak-Light Nonlinear Photonics Materials, and Tianjin Key Laboratory of Photonics Materials & Technology for Information Science, Nankai University, Tianjin 300457, China
  • Received:2005-11-25 Revised:2005-06-02 Online:2005-09-20 Published:2005-09-20
  • Supported by:
    Project supported by the National Natural Scientific foundation of China (Grant No 60178024) and the Cultivation Fund of the Key Scientific and Technical Innovation Project,Ministry of Education of China (Grant No 704012).

PDF (PC)

537

赞

摘要： The up-conversion luminescent property of the oxyfluoride glass ceramics 30SiO_{2}\cdot15Al_{2}O_{3}\cdot (50--x)PbF_{2}\cdot xCdF_{2} doped with 4ErF_{3}\cdot1YbF_{3} has been investigated. Up-conversion luminescent intensity of Er^{3+} ions increased obviously after heat-treatment due to co-doping with CdF_{2}. The structure model of nanocrystals Pb_{x}Cd_{1-x}F_{2} was determined and the effect of CdF_{2} in oxyfluoride glass ceramics was explained by the analysis of x-ray diffraction data. Different nucleation temperatures of samples with different compositions were obtained by differential thermal analysis curves and the results showed the growth process of different nanocrystals in glass ceramics.

关键词: up-conversion, glass ceramics, structure

Abstract: The up-conversion luminescent property of the oxyfluoride glass ceramics 30SiO2$\cdot$15Al2O3$\cdot$ (50--x)PbF2$\cdot$ xCdF2 doped with 4ErF3$\cdot$1YbF3 has been investigated. Up-conversion luminescent intensity of Er3+ ions increased obviously after heat-treatment due to co-doping with CdF2. The structure model of nanocrystals PbxCd1-xF2 was determined and the effect of CdF2 in oxyfluoride glass ceramics was explained by the analysis of x-ray diffraction data. Different nucleation temperatures of samples with different compositions were obtained by differential thermal analysis curves and the results showed the growth process of different nanocrystals in glass ceramics.

Key words: up-conversion, glass ceramics, structure

中图分类号:  (Glass-based composites, vitroceramics)

  • 81.05.Pj
78.55.Qr (Amorphous materials; glasses and other disordered solids) 61.46.Hk (Nanocrystals) 81.70.Pg (Thermal analysis, differential thermal analysis (DTA), differential thermogravimetric analysis) 61.05.cp (X-ray diffraction)