中国物理B ›› 2008, Vol. 17 ›› Issue (3): 1135-1137.doi: 10.1088/1674-1056/17/3/064

• • 上一篇    下一篇

Preparation and luminescence characteristics of Eu2+ activated silicate phosphor

李盼来, 杨志平, 王志军, 郭庆林   

  1. College of Physics Science & Technology, Hebei University, Baoding 071002, China
  • 收稿日期:2007-07-12 修回日期:2007-07-19 出版日期:2008-03-04 发布日期:2008-03-04
  • 基金资助:
    Project supported by Hebei Provincial Technology Development Foundation of China (Grant No 51215103b).

Preparation and luminescence characteristics of Eu2+ activated silicate phosphor

Li Pan-Lai(李盼来)†, Yang Zhi-Ping(杨志平), Wang Zhi-Jun(王志军), and Guo Qing-Lin(郭庆林)   

  1. College of Physics Science & Technology, Hebei University, Baoding 071002, China
  • Received:2007-07-12 Revised:2007-07-19 Online:2008-03-04 Published:2008-03-04
  • Supported by:
    Project supported by Hebei Provincial Technology Development Foundation of China (Grant No 51215103b).

PDF (PC)

969

赞

摘要： This paper synthesizes the Sr$_{2}$SiO$_{4}$\,:\,Eu$^{2 + }$ phosphor by high temperature solid-state reaction. The emission spectrum of Sr$_{2}$SiO$_{4}$\,:\,Eu$^{2 + }$ shows two bands centred at 480 and 547\,nm, which agree well with the calculation values of emission spectrum, and the location of yellow emission of Sr$_{2}$SiO$_{4}$\,:\,Eu$^{2 + }$ is influenced by the Eu$^{2 + }$ concentration. The excitation spectrum for 547\,nm emission has two bands at 363 and 402\,nm. The emission spectrum of white light emitting diodes (w-LEDs) based on Sr$_{2}$SiO$_{4}$\,:\,Eu$^{2 + }$ phosphor + InGaN LED was investigated.

关键词: white LED, Sr2SiO4:Eu2+, luminescence characteristics

Abstract: This paper synthesizes the Sr$_{2}$SiO$_{4}$:Eu$^{2 + }$ phosphor by high temperature solid-state reaction. The emission spectrum of Sr$_{2}$SiO$_{4}$:Eu$^{2 + }$ shows two bands centred at 480 and 547\,nm, which agree well with the calculation values of emission spectrum, and the location of yellow emission of Sr$_{2}$SiO$_{4}$:Eu$^{2 + }$ is influenced by the Eu$^{2 + }$ concentration. The excitation spectrum for 547 nm emission has two bands at 363 and 402 nm. The emission spectrum of white light emitting diodes (w-LEDs) based on Sr$_{2}$SiO$_{4}$:Eu$^{2 + }$ phosphor + InGaN LED was investigated.

Key words: white LED, Sr2SiO4:Eu2+, luminescence characteristics

中图分类号:  (Methods of materials synthesis and materials processing)

  • 81.20.-n
78.55.Hx (Other solid inorganic materials) 85.60.Jb (Light-emitting devices)