ANALYSIS OF THE LASER-INDUCED FLUORESCENCE IN CRYSTAL Cr:Mg2SiO4

郭祥义1, 杨宝成1, 沈国土1, 林远齐1, 祝生祥2, 潘佩聪3   

  1. (1)Department of Physics, East China Normal University, Shanghai 200062, China; (2)Department of Physics, Tongji University, Shanghai 200092, China; (3)Shanghai Institute of Ceramics, Academia Sinica, Shanghai 200050, China
  • 收稿日期:1993-08-26 出版日期:1994-06-20 发布日期:1994-06-20

ANALYSIS OF THE LASER-INDUCED FLUORESCENCE IN CRYSTAL Cr:Mg2SiO4

GUO XIANG-YI (郭祥义)a, YANG BAO-CHENG (杨宝成)a, SHEN GUO-TU (沈国土)a, LIN YUAN-QI (林远齐)a, ZHU SHENG-XIANG (祝生祥)b, PAN PEI-CONG (潘佩聪)c   

  1. a Department of Physics, East China Normal University, Shanghai 200062, China; b Department of Physics, Tongji University, Shanghai 200092, China; c Shanghai Institute of Ceramics, Academia Sinica, Shanghai 200050, China
  • Received:1993-08-26 Online:1994-06-20 Published:1994-06-20

PDF (PC)

417

赞

摘要： Observation of the 532 nm-laser-induced fluorescence spectra of two kinds of Cr:Mg2SiO4 crystalline samples grown in different atomsphere are reported. The experiments were con-ducted at both room temperature and liquid-nitrogen temperature. The fluorescence spectra of the two kinds of samples were different with respect to the polarizing direction of the inducing leser, and two emission bands with different polarized characters and various en-hancement in intensity at low temperatures were also found. In the light of the calculated results by Ms-Xα method, the main experimental results are explained.

Abstract: Observation of the 532 nm-laser-induced fluorescence spectra of two kinds of Cr:Mg2SiO4 crystalline samples grown in different atomsphere are reported. The experiments were con-ducted at both room temperature and liquid-nitrogen temperature. The fluorescence spectra of the two kinds of samples were different with respect to the polarizing direction of the inducing leser, and two emission bands with different polarized characters and various en-hancement in intensity at low temperatures were also found. In the light of the calculated results by Ms-X$\alpha$ method, the main experimental results are explained.

中图分类号:  (Other solid inorganic materials)

  • 78.55.Hx
81.10.Fq (Growth from melts; zone melting and refining) 61.72.S- (Impurities in crystals)