中国物理B ›› 2015, Vol. 24 ›› Issue (8): 87501-087501.doi: 10.1088/1674-1056/24/8/087501
• CONDENSED MATTER: ELECTRONIC STRUCTURE, ELECTRICAL, MAGNETIC, AND OPTICAL PROPERTIES • 上一篇 下一篇
李柱柏a, 兰剑亭a b, 张雪峰a b, 刘艳丽a b, 李永峰a b
Li Zhu-Bai (李柱柏)a, Lan Jian-Ting (兰剑亭)a b, Zhang Xue-Feng (张雪峰)a b, Liu Yan-Li (刘艳丽)a b, Li Yong-Feng (李永峰)a b
摘要: High energy ball milling (HEBM) is employed to produce nano-sized grains and particles. In this paper, the structure and magnetic properties are investigated in PrCo5 alloy for HEBM in an ethanol milling medium. With the increase of milling time, the grain size reduces and the coercivity increases. For a milling time of less than 30 min, the hysteresis loop of the aligned sample is very different from that of the un-aligned sample and it does not show a large decrease in magnetization slope, indicating a relatively good alignment of easy axes in particles due to the fact that the texture is nearly well preserved. However, when the milling time is further prolonged, the textured structure deteriorates in the powders. Even though exchange coupling exists between grains within the particle, the magnetic properties are exchange-decoupled between particles and the dipolar interaction results in a negative value of δ m in the whole range of the magnetic field.
中图分类号: (High coercivity materials)