Magnetization reversal in Fe48Pt34B34 magnetic foils

高有辉   

  1. Department of Physics, Beijing Normal University, Beijing 100875, China
  • 收稿日期:2011-04-18 修回日期:2011-05-17 出版日期:2011-10-15 发布日期:2011-10-15

Magnetization reversal in Fe48Pt34B34 magnetic foils

Gao You-Hui(高有辉)   

  1. Department of Physics, Beijing Normal University, Beijing 100875, China
  • Received:2011-04-18 Revised:2011-05-17 Online:2011-10-15 Published:2011-10-15

摘要: Exchange-spring magnet L1-FePt/(Fe2B+α-Fe) is fabricated by flash annealing a melt-spun Fe48Pt34B34 foil. A coercivity of 8500 Oe (1 Oe = 79.5775 A/m), squareness (Mr/Ms) of 0.70, saturation magnetization of 10.2 kGs (1 Gs = 10-4 T) and an effective anisotropy Keff =2.0 × 107 ergs/cm3 are obtained. A two-step magnetization reversal feature is characterized in this paper. An exchange bias phenomenon is also observed in a low saturation field.

Abstract: Exchange-spring magnet L1-FePt/(Fe2B+α-Fe) is fabricated by flash annealing a melt-spun Fe48Pt34B34 foil. A coercivity of 8500 Oe (1 Oe = 79.5775 A/m), squareness (Mr/Ms) of 0.70, saturation magnetization of 10.2 kGs (1 Gs = 10-4 T) and an effective anisotropy Keff =2.0 × 107 ergs/cm3 are obtained. A two-step magnetization reversal feature is characterized in this paper. An exchange bias phenomenon is also observed in a low saturation field.

Key words: L1-FePt, melt-spun, magnetic exchange interaction