Enhanced laser characteristics of pyrromethene 650 using modified PMMA as solid hosts

樊荣伟1, 夏元钦1, 陈德应1, 姜玉刚2   

  1. (1)National Key Laboratory of Science and Technology on Tunable Laser, Institute of optical-electronics, Harbin Institute of Technology, Harbin 150001 China; (2)National Key Laboratory of Science and Technology on Tunable Laser, Institute of optical-electronics, Harbin Institute of Technology, Harbin 150001 China; Tianjin Key Laboratory of Optical Thin Films, Tianjin Jinhang Institute of Technical Physics, Tianji
  • 收稿日期:2010-12-30 修回日期:2011-03-06 出版日期:2011-08-15 发布日期:2011-08-15
  • 基金资助:
    Project supported by the National Natural Science Foundation of China (Grant No. 61008023) and the Natural Scientific Research Innovation Foundation in Harbin Institute of Technology, China (Grant No. HIT.NSRIF.2009009).

Enhanced laser characteristics of pyrromethene 650 using modified PMMA as solid hosts

Fan Rong-Wei(樊荣伟)a), Jiang Yu-Gang(姜玉刚)a)b), Xia Yuan-Qin(夏元钦)a), and Chen De-Ying(陈德应)a)†   

  1. a National Key Laboratory of Science and Technology on Tunable Laser, Institute of optical-electronics, Harbin Institute of Technology, Harbin 150001 China; b Tianjin Key Laboratory of Optical Thin Films, Tianjin Jinhang Institute of Technical Physics, Tianjin 300192, China
  • Received:2010-12-30 Revised:2011-03-06 Online:2011-08-15 Published:2011-08-15
  • Supported by:
    Project supported by the National Natural Science Foundation of China (Grant No. 61008023) and the Natural Scientific Research Innovation Foundation in Harbin Institute of Technology, China (Grant No. HIT.NSRIF.2009009).

PDF (PC)

1014

赞

摘要： Solid-state samples based on modified polymethyl methacrylate (MPMMA) with methanol doped with the dye pyrromethene 650 (PM650) are prepared. The effects of a volume percentage of methanol on the laser characteristics of the sample, including spectra properties, slope efficiency, photostability and tunable properties, are investigated. The broadband dye laser output wavelength is around 655 nm and a highest slope efficiency of 32.23% is achieved. Pumping the samples at a repetition rate of 5 Hz with a pulse energy of as high as 100 mJ (the fluence is 0.26 J/cm2), the longest lifetime (168000 shots) is obtained in the sample (MMA:methanol=18:2), and the corresponding normalized photostability reaches 109.19 GJ/mol. When the sample (MMA:methanol=18:2) is placed in a Shoshan-type oscillator, the narrow-linewidth operation is a continuous tuning range (up to 64 nm). The results indicate that the laser characteristics of solid-state dyes can be greatly enhanced by using modified PMMA with methanol serving as the solid host.

关键词: solid-state dye laser, modified polymethyl methacrylate, pyrromethene 650, photostability, tunable properties

Abstract: Solid-state samples based on modified polymethyl methacrylate (MPMMA) with methanol doped with the dye pyrromethene 650 (PM650) are prepared. The effects of a volume percentage of methanol on the laser characteristics of the sample, including spectra properties, slope efficiency, photostability and tunable properties, are investigated. The broadband dye laser output wavelength is around 655 nm and a highest slope efficiency of 32.23% is achieved. Pumping the samples at a repetition rate of 5 Hz with a pulse energy of as high as 100 mJ (the fluence is 0.26 J/cm2), the longest lifetime (168000 shots) is obtained in the sample (MMA:methanol=18:2), and the corresponding normalized photostability reaches 109.19 GJ/mol. When the sample (MMA:methanol=18:2) is placed in a Shoshan-type oscillator, the narrow-linewidth operation is a continuous tuning range (up to 64 nm). The results indicate that the laser characteristics of solid-state dyes can be greatly enhanced by using modified PMMA with methanol serving as the solid host.

Key words: solid-state dye laser, modified polymethyl methacrylate, pyrromethene 650, photostability, tunable properties