Small-angle x-ray scattering study of the formation and growth of δ' in binary Al－7.87at% Li alloy

孟繁玲1, 王煜明1, 柴志刚2, 邹青3   

  1. (1)Institute of Materials Science, Jilin University, Changchun 130023, China; (2)Institute of Materials Science, Jilin University, Changchun 130023, China; Air Force Flying College in Changchun, Changchun 130022, China; (3)Machinery College, Jilin University, Changchun 130025, China
  • 收稿日期:2001-04-13 修回日期:2001-11-03 出版日期:2002-02-13 发布日期:2005-06-13

Small-angle x-ray scattering study of the formation and growth of $\delta'$ in binary Al－7.87at% Li alloy

Chai Zhi-Gang (柴志刚)ac, Meng Fan-Ling (孟繁玲)a, Zou Qing (邹青)b, Wang Yu-Ming (王煜明)a   

  1. a Institute of Materials Science, Jilin University, Changchun 130023, China; b Machinery College, Jilin University, Changchun 130025, China; c Air Force Flying College in Changchun, Changchun 130022, China
  • Received:2001-04-13 Revised:2001-11-03 Online:2002-02-13 Published:2005-06-13

PDF (PC)

329

赞

摘要： The formation and growth of δ' particles in an alloy of Al－7.87at% Li have been investigated using the small angle x-ray scattering technique. It has been shown that a transition zone, which exists between the δ' phase and the matrix after ageing for 16 h, disappears after ageing for 32 h. The existence of a transition zone indicates that the δ' phase is precipitated in the process of spinodal decomposition. This result also indicates that the growth of δ' particles should be divided into two stages. During the first stage, the δ' phase increases eating up the transition zone before ageing for 32 h, and in the second stage it grows by swallowing up each other after ageing for 32 h. In the latter stage, the larger and smaller δ' particles can coexist in the alloy.

Abstract: The formation and growth of $\delta'$ particles in an alloy of Al－7.87at% Li have been investigated using the small angle x-ray scattering technique. It has been shown that a transition zone, which exists between the $\delta'$ phase and the matrix after ageing for 16 h, disappears after ageing for 32 h. The existence of a transition zone indicates that the $\delta'$ phase is precipitated in the process of spinodal decomposition. This result also indicates that the growth of $\delta'$ particles should be divided into two stages. During the first stage, the $\delta'$ phase increases eating up the transition zone before ageing for 32 h, and in the second stage it grows by swallowing up each other after ageing for 32 h. In the latter stage, the larger and smaller $\delta'$ particles can coexist in the alloy.

Key words: Al－Li alloy, $\delta'$ phase, transition zone

中图分类号:  (X-ray scattering)

  • 78.70.Ck
81.40.Cd (Solid solution hardening, precipitation hardening, and dispersion hardening; aging)