Molecular dynamics simulations of dopant effectson lattice trapping of cracks in Ni matrix

Molecular dynamic analysis was performed on pure and doped (by Re, Ru, Co or W) Ni at 300 K using the embedded-atom-method (EAM) potentials to understand the crack formation of the doped Ni matrix in the (010)001 orientation. When Ni was doped with Re, Ru, and W, the matrix demonstrated increased lattice trapping limits and, as a result, improved the mechanical properties. Consequently, this prevented the bond breakage at the crack tips and promoted crack healing. The average atomic and surface energy values increased when Re, Ru, and W were added. Analysis of these energy increase helped us to understand the influence these elements had on the lattice trapping limits. The fracture strength of the Ni matrix at 300 K increased because of the formation of the stronger Ni-Re, Ni-Ru, and Ni-W bonds. At the same time, doping the Ni matrix with Co did not demonstrate any strengthening effects because of the formation of Co-Ni bonds, which are weaker than the Ni-Ni bonds. Out of all dopants tested in this work, Ni doping with W showed the best results.