Structures and optical properties of tungsten oxide thin films deposited by magnetron sputtering of WO₃ bulk：Effects of annealing temperatures

Tungsten oxide thin films were deposited on glass substrates by the magnetron sputtering of WO₃ bulk at room temperature. The deposited films were annealed at different temperatures in air. The structural measurements indicate that the films annealed below 300℃ were amorphous, while the films annealed at 400℃ were mixed crystalline with hexagonal and triclinic phases of WO₃. It was observed that the crystallization of the annealed films becomes more and more distinct with an increase in the annealing temperature. At 400℃, nanorod-like structures were observed on the film surface when the annealing time was increased from 60 min to 180 min. The presence of W=O stretching, W-O-W stretching, W-O-W bending and various lattice vibration modes were observed in Raman measurements. The optical absorption behaviors of the films in the range of 450-800 nm are very different with changing annealing temperatures from the room temperature to 400℃. After annealing at 400℃, the film becomes almost transparent. Increasing annealing time at 400℃ can lead to a small blue shift of the optical gap of the film.