Effect of microstructure on thermoelectric properties of CSD-grown Bi₂Sr₂Co₂O_y thin films

Three Bi₂Sr₂Co₂O_y thin films with different microstructures have been prepared by chemical solution deposition on LaAlO₃(001) through varying the annealing temperature. With the decrease in the annealing temperature, both the size and c-axis alignment degree of grains in the film decrease as well, leading to an increase in the film resistivity. In addition, the decrease in the annealing temperature also results in a slight increase in the seebeck coefficient due to the enhanced energy filtering effect of small-grain film. The nanostructured Bi₂Sr₂Co₂O_y film with the average grain size of about 100 nm shows a power factor comparable to that of the films with larger grains. Since the thermal conductivity of the nanostrcutured films can be depressed due to the enhanced phonon scattering by grain boundary, a higher figure of merit is expected in Bi₂Sr₂Co₂O_y thin film with grains in nanometer size.