Doctor-bladed Cu₂ZnSnS₄ light absorption layer for low-cost solar cell application

The doctor-blade method is investigated for the preparation of Cu₂ZnSnS₄ films for low-cost solar cell application. Cu₂ZnSnS₄ precursor powder, the main raw material for the doctor-blade paste, is synthesized by a simple ball-milling process. The doctor-bladed Cu₂ZnSnS₄ films are annealed in N₂ ambient under various conditions and characterized by X-ray diffraction, ultraviolent/vis spectrophotometry, scanning electron microscopy, and current-voltage (J-V) meansurement. Our experimental results indicate that (i) the X-ray diffraction peaks of the Cu₂ZnSnS₄ precursor powder each show a red shift of about 0.4°; (ii) the high-temperature annealing process can effectively improve the crystallinity of the doctor-bladed Cu₂ZnSnS₄, whereas an overlong annealing introduces defects; (iii) the band gap value of the doctor-bladed Cu₂ZnSnS₄ is around 1.41 eV; (iv) the short-circuit current density, the open-circuit voltage, the fill factor, and the efficiency of the best Cu₂ZnSnS₄ solar cell obtained with the superstrate structure of fluorine-doped tin oxide glass/TiO₂/In₂S₃/Cu₂ZnSnS₄/Mo are 7.82 mA/cm², 240 mV, 0.29, and 0.55%, respectively.