Luminescence characteristics of Eu³⁺ activated borate phosphor for white light emitting diode

In this paper, the Sr₃Y₂ (BO₃)₄:Eu³⁺ phosphor was synthesized by high temperature solid-state reaction method and the luminescence characteristics were investigated. The emission spectrum exhibits one strong red emission at 613nm corresponding to the electric dipole ⁵D₀--⁷F₂ transition of Eu³⁺ under 365nm excitation, this is because Eu³⁺ substituted for Y³⁺ occupied the non-centrosymmetric position in the crystal structure of Sr₃Y₂ (BO₃)₄. The excitation spectrum indicates that the phosphor can be effectively excited by ultraviolet (254nm, 365nm and 400nm) and blue (470nm) light. The effect of Eu³⁺ concentration on the red emission of Sr₃Y₂ (BO₃)₄:Eu³⁺ was measured, the result shows that the emission intensities increase with increasing Eu³⁺ concentration, then decrease. The Commission Internationale del'Eclairage chromaticity (x, y) of Sr₃Y₂(BO₃)₄:Eu³⁺ phosphor is (0.640,0.355) at 15 mol% Eu³⁺.