Magnetic properties and magnetoresistance effect of Y_1-xGd_xMn₆Sn₆ (x=0－1) compounds

The magnetic properties and magnetoresistance effect of Y_1-xGd_xMn₆Sn₆ (x=0－1) compounds have been investigated by magnetization and resistivity measurements in the applied field range (0－5 T). Compounds with x=0.4－1 display ferrimagnetic behaviours in the whole magnetic ordering temperature range, while compounds with x=0－0.2 display a field-induced metamagnetic transition, and the threshold fields decrease with increasing Gd content. The compounds with x=0.1－0.2 undergo an antiferromagnetic to ferromagnetic transition with increasing temperature. The cell-parameter a and c and cell-volume V of compounds (x=0－1) increase with increasing Gd content. It was found that the saturation magnetization M_s of the compounds (x=0.4－1) decreases, while the ordering points of the compounds (x=0－1)increase with increasing Gd content. A large MR effect was observed in the compound with x=0.2, and the maximum absolute value of MR at 5 K under 3 T is close to 19.3%.