Thermal effects and evolution of the defect concentration based on shear modulus relaxation data in a Zr-based metallic glass
Hao Qi1, Qiao Ji-Chao1, †, Goncharova E V2, Afonin G V2, Liu Min-Na1, Cheng Yi-Ting1, Khonik V A2
       

Temperature dependence of the shear modulus of Zr48(Cu5/6Ag1/6)44Al8 bulk metallic glass in the initial, relaxed and crystalline states measured at a heating rate of 3 K/min. The black solid and dashed curves are calculated using Eq. (3), in good agreement with the experimental data.