The atomic configurations of the nanocrystal Ti at different strains when the tension loading is perpendicular to prismatic plane II at 10 K for (a) ε = 9.2%, (b) ε = 9.8%, (c) ε = 16.9%, (d) ε = 17.8%, (e) ε = 21.1%, and (f) ε = 34.0%.