The atomic configurations of the nanocrystal Ti at different strains when the compression loading is normal to prismatic plane I at 10 K for (a) ε = 7.4%, (b) ε = 9.8%, (c) ε = 11.7%, (d) ε = 15.1%, (e) ε = 20.3%, and (f) ε = 24.3%.