(color online) Mechanical deformations of pure Σ9(114)/[110] Cu bicrystal and with different content values of Ni GB segregation, shearing along (a) and (b) at 10 K, respectively. Pure Cu structure was expressed as Cu (Cu–Ni base) because of the use of interatomic potential.