Structure dependence of magnetic properties in yttrium iron garnet by metal-organic decomposition method
Liu Yuan1, Wang Xiang2, Zhu Jie1, Huang Runsheng2, Tang Dongming1, †
       

Room temperature hysteresis loops of powders sintered at 1000 °C, 1050 °C, 1100 °C, 1150 °C, 1200 °C, 1250 °C, and 1300 °C. The low magnetic field parts of the curves are indicated as an inset figure to make clear the change of coercivity.