Synthesis and study the influence of yttrium doping on band structure, optical, non-linear optical and dielectric results for Ca12Al14O33 (C12A7) single crystals grown using traveling-solvent floating zone (TSFZ) method

doi:10.1088/1674-1056/ac0a5f

中国物理B ›› 2022, Vol. 31 ›› Issue (1): 18103-018103.doi: 10.1088/1674-1056/ac0a5f

Synthesis and study the influence of yttrium doping on band structure, optical, non-linear optical and dielectric results for Ca₁₂Al₁₄O₃₃ (C12A7) single crystals grown using traveling-solvent floating zone (TSFZ) method

A. Abdel Moez^1,†, Ahmed I. Ali², and A. Tayel²

1 Solid State Physics Department, Physical Research Division, National Research Centre(NRC), 33 El Bohouth Street, Dokki, Giza 12622, Egypt;
2 Basic Science Department, Faculty of Faculty of Technology and Education, Helwan University, Kobry El-Qopa, Cairo 11281, Egypt

收稿日期:2021-04-15 修回日期:2021-05-17 接受日期:2021-06-11 出版日期:2021-12-03 发布日期:2021-12-14
通讯作者: A. Abdel Moez E-mail:aam692003@yahoo.com

Synthesis and study the influence of yttrium doping on band structure, optical, non-linear optical and dielectric results for Ca₁₂Al₁₄O₃₃ (C12A7) single crystals grown using traveling-solvent floating zone (TSFZ) method

A. Abdel Moez^1,†, Ahmed I. Ali², and A. Tayel²

1 Solid State Physics Department, Physical Research Division, National Research Centre(NRC), 33 El Bohouth Street, Dokki, Giza 12622, Egypt;
2 Basic Science Department, Faculty of Faculty of Technology and Education, Helwan University, Kobry El-Qopa, Cairo 11281, Egypt

Received:2021-04-15 Revised:2021-05-17 Accepted:2021-06-11 Online:2021-12-03 Published:2021-12-14
Contact: A. Abdel Moez E-mail:aam692003@yahoo.com

摘要/Abstract

摘要： Ca₁₂Al₁₄O₃₃ (C12A7) and Y_0.02Ca_11.98Al₁₄O₃₃ (Y-C12A7) single crystals were grown by using the traveling-solvent floating zone (TSFZ) method. The temperature was increased to avoid the bubbles and cracks which may be formed during the preparation of the ingot material. We have started with the flux higher than the normal to avoid the bubbles and make good treatment for the solid-liquid interface. The structures of both Ca₁₂Al₁₄O₃₃ (C12A7) and Y_0.02Ca_11.98Al₁₄O₃₃ (Y-C12A7) were studied by using x-ray diffraction (XRD). Optical properties for C12A7 and Y-C12A7 single crystals have been studied in order to determine the optical parameters such as optical energy gap (E_g), refractive index n, oscillating energy (E_o), dispersion energy (E_d), volume energy loss function (VELF), and surface energy loss function (SELF). Finally, a new result for these samples is that the third-order nonlinear optical susceptibility (χ⁽³⁾) was determined. The results have been discussed with effect of Y-doping on the C12A7 single crystals for optical and industrial applications.

关键词: syntheses Ca₁₂Al₁₄O₃₃ (C12A7) single crystals, Y-doping, optical parameters, dielectric results, nonlinear optical susceptibility

Abstract: Ca₁₂Al₁₄O₃₃ (C12A7) and Y_0.02Ca_11.98Al₁₄O₃₃ (Y-C12A7) single crystals were grown by using the traveling-solvent floating zone (TSFZ) method. The temperature was increased to avoid the bubbles and cracks which may be formed during the preparation of the ingot material. We have started with the flux higher than the normal to avoid the bubbles and make good treatment for the solid-liquid interface. The structures of both Ca₁₂Al₁₄O₃₃ (C12A7) and Y_0.02Ca_11.98Al₁₄O₃₃ (Y-C12A7) were studied by using x-ray diffraction (XRD). Optical properties for C12A7 and Y-C12A7 single crystals have been studied in order to determine the optical parameters such as optical energy gap (E_g), refractive index n, oscillating energy (E_o), dispersion energy (E_d), volume energy loss function (VELF), and surface energy loss function (SELF). Finally, a new result for these samples is that the third-order nonlinear optical susceptibility (χ⁽³⁾) was determined. The results have been discussed with effect of Y-doping on the C12A7 single crystals for optical and industrial applications.

Key words: syntheses Ca₁₂Al₁₄O₃₃ (C12A7) single crystals, Y-doping, optical parameters, dielectric results, nonlinear optical susceptibility

中图分类号: (Specific materials: fabrication, treatment, testing, and analysis)

81.05.-t

A. Abdel Moez, Ahmed I. Ali, and A. Tayel. Synthesis and study the influence of yttrium doping on band structure, optical, non-linear optical and dielectric results for Ca₁₂Al₁₄O₃₃ (C12A7) single crystals grown using traveling-solvent floating zone (TSFZ) method[J]. 中国物理B, 2022, 31(1): 18103-018103.

参考文献

[1] Exarhos G J and Zhou X D 2007 Thin Solid Films 515 7025
[2] Hosono H 2007 Thin Solid Films 515 6000
[3] Jonas S, Nadachowski F and Szwagierczak D 1999 Ceram. Int. 25 77
[4] Aitasalo T, Holsa J, Jungner H, Lastusaari M, Niittykoski J, Parkkinen M and Valtonen R 2004 Opt. Mater. 26 113
[5] Dongdong J 2006 J. Lumin. 117 170
[6] Murayama Y 1999 Luminous Paints (Boca Raton: Phosphor Handbook, CRC Press)
[7] Kang E T, Lee S J and Hannon A C 2006 J. Non Cryst. Solids 352 725
[8] Sampaio J A, Gama S, Baesso M L and Catunda T 2005 J. Non Cryst. Solids 351 1594
[9] Sampaio J A, Catunda T, Coelho A A, Gama S, Bento A C, Miranda L C M and BaessoM L 2000 J. Non Cryst. Solids 273 239
[10] Mazin I I and Papaconstantopoulos D A 2004 Phys. Rev. B 69 180512
[11] Kalita S J, Bose S, Bandyopadhyay A and Hosick H L 2002 J. Mater. Res. 17 3042
[12] Watauchi S, Tanaka I, Hayashi K, Hirano M and Hosono H 2002 J. Cryst. Grow. 237-239 801
[13] Toldsepp E, Avarmaa T, Denks V, Feldbach E, Kirm M, Maaroos A, Mandar H and Vielhauer S 2010 Optic. Mater. 32 784
[14] Gong L, Lin Z, Ning S, Sun J, Shen J, Torimoto Y and Li Q 2010 Mater. Lett. 64 1322
[15] Yuan X, Xu Y and He Y 2007 J. Alloys Compd. 441 251
[16] Jeevaratnam J, Glasser F P and Glasser L S D 1964 J. Am. Ceram. Soc. 47 105
[17] Lacerada M, Irvine J T S, Lachowski E E, Glasserand E P and West A R 1988 Trans. J. 87 191
[18] Hosono H, Hayashi K, Kajihara K, Sushko P V and Shluger A L 2009 Sol. Stat. Ion. 180 550
[19] Matsuishi S, Hayashi K, Hirano M and Hosono H 2005 J. Am. Chem. Soc. 127 12454
[20] Liu X L, Liu Y X, Yan D T, Zhu H C, Liu C G, Xu C S, Liu Y C and Wang X J 2012 J. Mater. Chem. 22 16839
[21] Bartl H and Scheller T 1970 Mineral. Monatshefte 35 547
[22] Christensen A N 1987 Acta Chem. Scand. 41a 110
[23] Strandbakke R, Kongshaug C, Haugsrud R and Norby T 2009 J. Phys. Chem. C 113 8938
[24] Lee D K, Kogel L, Ebbinghaus S G, Valov I, Wiemhoefer H D, Lerch M and Janek J 2009 Phys. Chem. Chem. Phys. 11 3105
[25] Janek J and Lee D K 2010 J. Korean Ceram. Soc. 47 99
[26] Li Q X, Hayashi K, Nishioka M, Kashiwagi H, Hirano M, Torimoto Y, Hosono H and Sadakata M 2002 Appl. Phys. Lett. 80 4259
[27] Labidi M, Labidi S, Ghemid S, Meradji H and El Haj Hassan F 2010 Phys. Scr. 82 045605
[28] Hosono H, Asada N and Abe Y 1990 J. Appl. Phys. 67 2840
[29] Dan W, Yuxue L, Changshan X, Yichun L, Guorui W and Xinghua L 2008 J. Rar. Eaths. 26 433
[30] Park Y J and Kim Y J 2008 Ceram. Inter. 34 1109
[31] Zhu H, Liu Y, Yan D, Bian H, Li S, Liu C, Xu C and Wang X 2014 Opt. Mater. 36 1771
[32] Singh V, Chakradhar R P S, Ledoux-Rak I, Badie L, Pelle F and Ivanova S 2009 J. Lumin. 129 1375
[33] Ju H, Su X, Xu S, Zhang Y, Deng D, Zhao S, Wang H, Wang B and Sun L 2009 Mater. Lett. 63 1275
[34] Lin Y, Tang Z, Zhang Z and Nan C 2003 J. Europ. Ceram. Soc. 23 175
[35] Kumar A S, Kumar R A, Balasundaraprabhu R, Senthil K, Kumar S R and Gunasekaran V 2015 Spectrochim. Acta A 134 283
[36] Rui W, Yushen Z, Jinchao S, Liang L and Yanling X 2011 J. Rar. Eaths 29 826
[37] Verma R K and Rai S B 2013 Chem. Phys. Lett. 559 71
[38] Park J, Kim G and Kim Y J 2013 Ceram. Inter. 39 S623
[39] Brika M G, Pan Y X and Liu G K 2011 J. Alloys Compd. 509 1452
[40] Murata T, Tanoue T, Iwasaki M, Morinaga K and Hase T 2005 J. Lumin. 114 207
[41] Meng L, Meng H, Gog W, Liu W and Zhang Z 2011 Thin Solid Films 519 7627
[42] Badr Y, Battisha I K, El Nahrawy A M S, Elouadi B and Kamal M 2011 New Journal of Glass and Ceramics 1 71
[43] Gu F., Wang S F, Lu M K, Zhou G J, Xu D and Yuan D R 2004 J. Phys. Chem. B 108 8119
[44] Khan Z R, Zulfequar M and Khan M S 2010 Mater. Sci. Eng. B 174 145
[45] Aranda J, Morenza J L, Esteve J and Codina J M 1984 Thin Solid Films 120 23
[46] Fadel M, Fayek S A, Abou-Helal M O, Ibrahium M M and Shakra A M 2009 J. Alloys Compd. 485 604
[47] Pankove J I 1971 Optical Process in Semiconductors (New York: Dover Publications)
[48] Torris J, Cisneros J I, Gordillo G and Alvarez F 1996 Thin Solid Films 289 238
[49] Ali A I, Ammar A H and Abdel Moez A 2014 Superlatt. Microstruct. 65 285
[50] El mandouh Z El Sayed, Elmeleegi H A and Abdel Moez A 2014 Turk. J. Phys. 38 145
[51] Marquez E, Bernal-Oliva A M, Gonzalez-Leal J M, Prieto-Alcon R, Ledesma A, Jimenez-Garay R and Márti I 1999 Mater. Chem. Phys. 60 231
[52] M El-Nahass M, Ammar A H, Farag A A M, Atta A A and El-Zaidia E F M 2011 Sol. Stat. Sci. 13 596
[53] Djurisic A B and Li E H 1998 Opt. Commun. 157 72
[54] Ali A I, Son J Y, Ammar A H, Abdel Moez A and Kim Y S 2013 Results Phys. 3 167
[55] Ziabari A A and Ghodsi F E 2011 J. Alloys Compd. 509 8748

Synthesis and study the influence of yttrium doping on band structure, optical, non-linear optical and dielectric results for Ca₁₂Al₁₄O₃₃ (C12A7) single crystals grown using traveling-solvent floating zone (TSFZ) method

Synthesis and study the influence of yttrium doping on band structure, optical, non-linear optical and dielectric results for Ca₁₂Al₁₄O₃₃ (C12A7) single crystals grown using traveling-solvent floating zone (TSFZ) method

RichHTML

PDF (PC)

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 1

Metrics

本文评价

推荐阅读 0