Synthesis of Au nanorods in a low pH solution via seed-media method

马晓a, 冯晋阳a, 游芳芳a, 马娟b, 赵修建a, 王木琴c   

  1. a State Key Laboratory of Silicate Materials for Architectures (Wuhan University of Technology), Wuhan 430070, China;
    b Faculty of Geomatics Engineering, Kunming Metallurgy College, Kunming 650033, China;
    c Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, Taiwan, China
  • 收稿日期:2013-09-04 修回日期:2013-12-23 出版日期:2014-08-15 发布日期:2014-08-15
  • 基金资助:
    Project supported by the Nippon Sheet Glass Foundation for Materials Science and Engineering (Japan, January 2012) and the Natural Science Foundation of Hubei Province of China (Grant No. 2011CDB426).

Synthesis of Au nanorods in a low pH solution via seed-media method

Ma Xiao (马晓)a, Feng Jin-Yang (冯晋阳)a, You Fang-Fang (游芳芳)a, Ma Juan (马娟)b, Zhao Xiu-Jian (赵修建)a, Wang Moo-Chin (王木琴)c   

  1. a State Key Laboratory of Silicate Materials for Architectures (Wuhan University of Technology), Wuhan 430070, China;
    b Faculty of Geomatics Engineering, Kunming Metallurgy College, Kunming 650033, China;
    c Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, Taiwan, China
  • Received:2013-09-04 Revised:2013-12-23 Online:2014-08-15 Published:2014-08-15
  • Contact: Feng Jin-Yang, Zhao Xiu-Jian, Wang Moo-Chin E-mail:fjy@whut.edu.cn;opules@whut.edu.cn;mcwang@kmu.edu.tw
  • Supported by:
    Project supported by the Nippon Sheet Glass Foundation for Materials Science and Engineering (Japan, January 2012) and the Natural Science Foundation of Hubei Province of China (Grant No. 2011CDB426).

PDF (PC)

490

赞

摘要： The gold (Au) nanorods with various aspect ratios are obtained by a seed-media method in low pH growth solution. Transmission electron microscopy (TEM) and UV-visible spectrophotometry are utilized to characterize the Au nanorods, and the longitudinal absorption peak positions of Au nanorods show different shifting trends of the growth evolutions in various low pH (1～ 3) solutions. Other influential factors on the shape of Au nanorod are also systematically studied under low pH reaction condition. The positions of longitudinal peak shift between 600 nm and 900 nm, with the aspect ratios of Au nanorods varying from 2 to 5 both in the simulation and experimental results. The simulation results are in agreement with experimental ones.

关键词: Au nanorods, seed-media method, aspect ratio, surface plasmon absorption

Abstract: The gold (Au) nanorods with various aspect ratios are obtained by a seed-media method in low pH growth solution. Transmission electron microscopy (TEM) and UV-visible spectrophotometry are utilized to characterize the Au nanorods, and the longitudinal absorption peak positions of Au nanorods show different shifting trends of the growth evolutions in various low pH (1～ 3) solutions. Other influential factors on the shape of Au nanorod are also systematically studied under low pH reaction condition. The positions of longitudinal peak shift between 600 nm and 900 nm, with the aspect ratios of Au nanorods varying from 2 to 5 both in the simulation and experimental results. The simulation results are in agreement with experimental ones.

Key words: Au nanorods, seed-media method, aspect ratio, surface plasmon absorption