Infrared-to-green upconversion luminescence and mechanism of Ho3+, Nd3+ and Yb3+ ions in oxyfluoride glass ceramics

张军杰, 戴世勋   

  1. Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China
  • 收稿日期:2003-11-21 修回日期:2004-01-16 出版日期:2004-07-05 发布日期:2005-07-05
  • 基金资助:
    Project supported by the National Natural Science Foundation of China (Grant No 60207006), and by the Optical Science and Technology of Shanghai (Grant No 022261046).

Infrared-to-green upconversion luminescence and mechanism of Ho3+, Nd3+ and Yb3+ ions in oxyfluoride glass ceramics

Zhang Jun-Jie (张军杰)a, Kawamoto Yojib, Dai Shi-Xun(戴世勋)a   

  1. a Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China; b Department of Chemistry, Faculty of Science, Kobe University, Rokkodai, Nada, Kobe 657-8501, Japan
  • Received:2003-11-21 Revised:2004-01-16 Online:2004-07-05 Published:2005-07-05
  • Supported by:
    Project supported by the National Natural Science Foundation of China (Grant No 60207006), and by the Optical Science and Technology of Shanghai (Grant No 022261046).

PDF (PC)

446

赞

摘要： New oxyfluoride glasses and glass ceramics co-doped with Nd^{3+}, Yb^{3+} and Ho^{3+} were prepared. The upconversion of infrared radiation into green fluorescence has been studied for Nd^{3+}, Yb^{3+} and Ho^{3+} in the transparent oxyfluoride glass ceramics. At room temperature very strong green upconversion luminescence due to the Ho^{3+}: ({}^5F_4, {}^5S_2)→{}^5I_8 transition under 800 nm excitation was observed in the glass ceramics. The intensity of the green upconversion luminescence in a 1mol% YbF_3-containing glass ceramic was found to be about 120 times stronger than that in the precursor oxyfluoride glass. The reason for the highly efficient Ho^{3+} upconversion luminescence in the oxyfluoride glass ceramics is discussed. The upconversion mechanism is also investigated.

关键词: upconversion, mechanism, oxyfluoride glass ceramics

Abstract: New oxyfluoride glasses and glass ceramics co-doped with Nd$^{3+}$, Yb$^{3+}$ and Ho$^{3+}$ were prepared. The upconversion of infrared radiation into green fluorescence has been studied for Nd$^{3+}$, Yb$^{3+}$ and Ho$^{3+}$ in the transparent oxyfluoride glass ceramics. At room temperature very strong green upconversion luminescence due to the Ho$^{3+}$: ($^5$F$_4$, $^5$S$_2$)→$^5$I$_8$ transition under 800 nm excitation was observed in the glass ceramics. The intensity of the green upconversion luminescence in a 1mol% YbF$_3$-containing glass ceramic was found to be about 120 times stronger than that in the precursor oxyfluoride glass. The reason for the highly efficient Ho$^{3+}$ upconversion luminescence in the oxyfluoride glass ceramics is discussed. The upconversion mechanism is also investigated.

Key words: upconversion, mechanism, oxyfluoride glass ceramics

中图分类号:  (Other solid inorganic materials)

  • 78.55.Hx
81.05.Pj (Glass-based composites, vitroceramics) 81.40.Gh (Other heat and thermomechanical treatments)