Chin. Phys. B, 2017, Vol. 26(12): 128103    DOI: 10.1088/1674-1056/26/12/128103
INTERDISCIPLINARY PHYSICS AND RELATED AREAS OF SCIENCE AND TECHNOLOGY Prev   Next  

Optical properties of wavelength-tunable green-emitting color conversion glass ceramics

Yang Li(李杨)1,2,3, Li-Li Hu(胡丽丽)1, Bo-Bo Yang(杨波波)4, Ming-Ming Shi(石明明)4, Jun Zou(邹军)4
1. Key Laboratory of Materials for High Power Laser, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China;
2. University of Chinese Academy of Sciences, Beijing 100049, China;
3. School of Materials Science and Engineering, Shanghai Institute of Technology, Shanghai 201418, China;
4. School of Science, Shanghai Institute of Technology, Shanghai 201418, China
Abstract  

Color conversion glass ceramics are prepared by cosintering borosilicate glass frits and green 0.06Ce:Y2.94(Al1-xGax)5O12 phosphors. The crystal structures, the influence of Ga concentration on the photoluminescence (PL), and reliability properties of the color conversion glass ceramics are investigated. The PL emission wavelengths of 0.06Ce:Y2.94(Al1-xGax)5O12 glass ceramics show blue shift from 545 nm to 525 nm with increasing Ga content (x value) under excited at 460 nm. Reliability test results show that the quantum yield (QY) of 0.06Ce:Y2.94(Al1-xGax)5O12 glass ceramics decreases from 70.60% to 59.06% with x value increasing from 0.15 to 0.35 under the ambient condition of 85℃/RH85% for the exposure time of 168 h. And the quantum yield (QY) of 0.06Ce:Y2.94(Al1-xGax)5O12 glass ceramics decreases from 65.13% to 52.23% after being soaked into boiled water for 4 h. The finding reveals that the addition of Ga can deteriorate the reliability of the color conversion glass ceramics.

Keywords:  color conversion glass ceramic      photoluminescence wavelength      quantum yield      reliability property  
Received:  21 July 2017      Revised:  13 September 2017      Accepted manuscript online: 
PACS:  81.05.Kf (Glasses (including metallic glasses))  
  42.70.Ce (Glasses, quartz)  
Fund: 

Project supported by the National Natural Science Foundation of China (Grant No. 51302171), the Science and Technology Commission of Shanghai Municipality, China (Grant No. 14500503300), and the Natural Science Foundation of Shanghai, China (Grant No. 12ZR1430900).

Corresponding Authors:  Yang Li, Yang Li     E-mail:  liyang123@sit.edu.cn;hulili@siom.ac.cn

Cite this article: 

Yang Li(李杨), Li-Li Hu(胡丽丽), Bo-Bo Yang(杨波波), Ming-Ming Shi(石明明), Jun Zou(邹军) Optical properties of wavelength-tunable green-emitting color conversion glass ceramics 2017 Chin. Phys. B 26 128103

[1] Guo X, Liu Q L, Li C, Liu B, Dong J and Shen G D 2015 Chin. Phys. B 24 068505
[2] Feng B, Deng B, Liu L G, Li Z C, Feng M X, Zhao H M and Sun Q 2017 Acta Phys. Sin. 66 047801(in Chinese)
[3] Fu M, Wen S S, Xia Y Y, Xiang C M, Ma B X and Fang F 2017 Acta Phys. Sin. 66 048501(in Chinese)
[4] Chen D Q, Xu W, Zhou Y, Zhong J S and Li S C 2017 J. Mater. Chem. C 5 738
[5] Xu W, Chen D Q, Yuan S, Zhou Y and Li S C 2017 Chem. Eng. J. 317 854
[6] Zhou Y, Chen D Q, Tian W D and Ji Z G 2015 J. Am. Ceram. Soc. 98 2445
[7] Iqbal F, Kim S and Kim H 2017 Opt. Mater. 72 323
[8] Yie H, Kim S, Kim Y and Kim H 2017 J. Non-Cryst. Solids 463 19
[9] Tsai C C 2015 Optik-International Journal for Light and Electron Optics 126 655
[10] Chen D Q, Xiang W D, Liang X J, Zhong J S, Yu H, Ding M Y, Lu H W and Ji Z G 2015 J. Eur. Ceram. Soc. 35 859
[11] Zhu Q Q, Wang X J, Wang L, Hirosaki N, Nishimura T, Tian Z F, Li Q, Xu Y Z, Xu X and Xie R J 2015 J. Mater. Chem. C 3 10761
[12] Jeong H J, Huh C, Lim T Y, Kim J H, Lee M J, Jeon D W, Hwang J H, Park T H and Shin D W 2015 J. Non-Cryst. Solids 423-424 25
[13] Zhu Q Q, Xu X, Wang L, Tian Z F, Xu Y Z, Hirosaki N and Xie R J 2017 J. Alloys Compd. 702 193
[14] Han K, Lee S, Choi Y, Im W and Chung W 2016 J. Non-Cryst. Solids 445-446 77
[15] Yang B B, Zou J, Wang F C, Zhang C Y, Xu J Y, Li L and Sun L H 2016 J. Mater. Sci.-Mater. Electron. 27 3376
[16] Ji E K, Song Y H, Lee M J and Yoon D H 2015 Mater. Lett. 157 89
[17] Zhong J S, Chen D Q, Zhou Y, Wan Z Y Ding M Y and Ji Z G 2016 J. Eur. Ceram. Soc. 36 1705
[18] Shannon R D 1993 J. Appl. Phys. 73 348
[19] Pan Y X, Wu M M and Su Q 2004 J. Phys. Chem. Solid 65 845
[1] Absorption, quenching, and enhancement by tracer in acetone/toluene laser-induced fluorescence
Guang Chang(常光), Xin Yu(于欣), Jiangbo Peng(彭江波), Yang Yu(于杨), Zhen Cao(曹振), Long Gao(高龙), Minghong Han(韩明宏), and Guohua Wu(武国华). Chin. Phys. B, 2020, 29(12): 124212.
[2] Effect of sintering temperature on luminescence properties of borosilicate matrix blue-green emitting color conversion glass ceramics
Qiao-Yu Zheng(郑巧瑜), Yang Li(李杨), Wen-Juan Wu(吴文娟), Ming-Ming Shi(石明明), Bo-Bo Yang(杨波波), Jun Zou(邹军). Chin. Phys. B, 2019, 28(10): 108102.
[3] Comparison of the photoemission behaviour between negative electron affinity GaAs and GaN photocathodes
Zhang Yi-Jun(张益军), Zou Ji-Jun(邹继军), Wang Xiao-Hui(王晓晖), Chang Ben-Kang(常本康), Qian Yun-Sheng(钱芸生), Zhang Jun-Ju(张俊举), and Gao Pin(高频) . Chin. Phys. B, 2011, 20(4): 048501.
[4] Improvement of photoemission performance of a gradient-doping transmission-mode GaAs photocathode
Zhang Yi-Jun(张益军), Niu Jun(牛军), Zhao Jing(赵静), Xiong Ya-Juan(熊雅娟),Ren Ling(任玲), Chang Ben-Kang(常本康), and Qian Yun-Sheng(钱芸生) . Chin. Phys. B, 2011, 20(11): 118501.
No Suggested Reading articles found!