Chin. Phys. B, 2014, Vol. 23(8): 087802    DOI: 10.1088/1674-1056/23/8/087802
SPECIAL TOPI—International Conference on Nanoscience & Technology, China 2013 Prev   Next  

Thickness dependence of the optical constants of oxidized copper thin films based on ellipsometry and transmittance

Gong Jun-Bo (宫俊波)a, Dong Wei-Le (董伟乐)a, Dai Ru-Cheng (代如成)b, Wang Zhong-Ping (王中平)b, Zhang Zeng-Ming (张增明)b, Ding Ze-Jun (丁泽军)a
a Department of Physics, University of Science and Technology of China, Hefei 230026, China;
b The Center of Physical Experiments, University of Science and Technology of China, Hefei 230026, China
Abstract  Thin oxidized copper films in various thickness values are deposited onto quartz glass substrates by electron beam evaporation. The ellipsometry parameters and transmittance in a wavelength range of 300 nm-1000 nm are collected by a spectroscopic ellipsometer and a spectrophotometer respectively. The effective thickness and optical constants, i.e., refractive index n and extinction coefficient k, are accurately determined by using newly developed ellipsometry combined with transmittance iteration method. It is found that the effective thickness determined by this method is close to the physical thickness and has obvious difference from the mass thickness for very thin film due to variable density of film. Furthermore, the thickness dependence of optical constants of thin oxidized Cu films is analyzed.
Keywords:  thin film      optical constants      thickness      copper  
Received:  04 September 2013      Revised:  20 March 2014      Accepted manuscript online: 
PACS:  78.20.Ci (Optical constants (including refractive index, complex dielectric constant, absorption, reflection and transmission coefficients, emissivity))  
  68.47.Gh (Oxide surfaces)  
  68.55.jd (Thickness)  
  68.47.De (Metallic surfaces)  
Fund: Project supported by the National Natural Science Foundation of China (Grant Nos. 11074232, 10874160, and 21002097) and the National Basic Research Program of China (Grant Nos. 2011CB932801 and 2012CB933702).
Corresponding Authors:  Zhang Zeng-Ming     E-mail:  zzm@ustc.edu.cn

Cite this article: 

Gong Jun-Bo (宫俊波), Dong Wei-Le (董伟乐), Dai Ru-Cheng (代如成), Wang Zhong-Ping (王中平), Zhang Zeng-Ming (张增明), Ding Ze-Jun (丁泽军) Thickness dependence of the optical constants of oxidized copper thin films based on ellipsometry and transmittance 2014 Chin. Phys. B 23 087802

[1] Brimhall N, Herrick N, Allred D D, Turley R S, Ware M and Peatross J 2009 Opt. Express 17 23873
[2] Ramanandan G K P, Ramakrishnan G and Planken P C M 2012 J. Appl. Phys. 111 123517
[3] Huang Y, Ye H A, Li S Q and Dou Y F 2013 Chin. Phys. B 22 027301
[4] Boggio J E 1979 J. Chem. Phys. 70 5054
[5] Suzuki S, Ishikawa Y, Isshiki M and Waseda Y 1997 Mater. Trans. 38 1004
[6] Oreilly M, Jiang X, Beechinor J T, Lynch S, Nidheasuna C, Patterson J C and Crean G M 1995 Appl. Surf. Sci. 91 152
[7] Iijima J, Lim J W, Hong S H, Suzuki S, Mimura K and Isshiki A 2006 Appl. Surf. Sci. 253 2825
[8] Zhong C, Jiang Y M, Luo Y F, Deng B, Zhang L and Li J 2008 Appl. Phys. A 90 263
[9] Njeh A, Wieder T and Fuess H 2002 Surf. Interface Anal. 33 626
[10] Chaudhari M B, Mohammed W S, Hornyak G L and Dutta J 2012 Micro Nano Lett. 7 146
[11] Lecohier B, Calpini B, Philippoz J M, Vandenbergh H, Laub D and Buffat P A 1993 J. Electrochem. Soc. 140 789
[12] Li Z W and Gordon R G 2006 Chem. Vapor Depos. 12 435
[13] Ray S C 2001 Sol. Energ. Mater. Sol. Cells 68 307
[14] Zhao Q X, Bian F, Zhou Y, Gao Y F, Wang S B, Ma L, Yan Z and Liu B T 2008 Mater. Lett. 62 4140
[15] Zhang J T, Li Y, Luo Z Y and Wu X J 2010 Chin. Phys. Lett. 27 050601
[16] Gong H F, Lu W, Wang L M and Li G P 2012 Chin. Phys. B 21 113601
[17] Elizalde E, Frigerio J M and Rivory J 1986 Appl. Opt. 25 4557
[18] Gong J B, Dai R C, Wang Z P, Zhang Z M and Ding Z J (to be submitted)
[19] Hass G and Hadley L 1963 American Institute of Physics Handbook, Section 6g: Optical Properties of Metals, 2nd edn. (New York: McGraw-Hill) p. 103
[20] Ghijsen J, Tjeng L H, van Elp J, Eskes H, Westerink J, Sawatzky G A and Czyzyk M T 1988 Phys. Rev. B 11 322
[21] Honjo G 1949 J. Phys. Soc. Jpn. 4 352
[22] Palik D 1985 Handbook of Optical Constants of Solids (New York: Academic Press)
[23] Singh J 2006 Optical Properties of Condensed Matter and Applications (Hoboken: John Wiley & Sons Inc.) p. 32
[24] Sennett R S and Scott G D 1950 J. Opt. Soc. Am. 40 203
[25] Zhou Y M, He Y G, Lu A X and Wan Q 2009 Chin. Phys. B 18 3966
[26] Surholt T, Mishin Y M and Herzig C 1994 Phys. Rev. B 50 3577
[1] High repetition granular Co/Pt multilayers with improved perpendicular remanent magnetization for high-density magnetic recording
Zhi Li(李智), Kun Zhang(张昆), Ao Du(杜奥), Hongchao Zhang(张洪超), Weibin Chen(陈伟斌), Ning Xu(徐宁), Runrun Hao(郝润润), Shishen Yan(颜世申), Weisheng Zhao(赵巍胜), and Qunwen Leng(冷群文). Chin. Phys. B, 2023, 32(2): 026803.
[2] Method of measuring one-dimensional photonic crystal period-structure-film thickness based on Bloch surface wave enhanced Goos-Hänchen shift
Yao-Pu Lang(郎垚璞), Qing-Gang Liu(刘庆纲), Qi Wang(王奇), Xing-Lin Zhou(周兴林), and Guang-Yi Jia(贾光一). Chin. Phys. B, 2023, 32(1): 017802.
[3] Migration of weakly bonded oxygen atoms in a-IGZO thin films and the positive shift of threshold voltage in TFTs
Chen Wang(王琛), Wenmo Lu(路文墨), Fengnan Li(李奉南), Qiaomei Luo(罗巧梅), and Fei Ma(马飞). Chin. Phys. B, 2022, 31(9): 096101.
[4] Erratum to “Accurate determination of film thickness by low-angle x-ray reflection”
Ming Xu(徐明), Tao Yang(杨涛), Wenxue Yu(于文学), Ning Yang(杨宁), Cuixiu Liu(刘翠秀), Zhenhong Mai(麦振洪), Wuyan Lai(赖武彦), and Kun Tao(陶琨). Chin. Phys. B, 2022, 31(9): 099901.
[5] Novel closed-cycle reaction mode for totally green production of Cu1.8Se nanoparticles based on laser-generated Se colloidal solution
Zhangyu Gu(顾张彧), Yisong Fan(范一松), Yixing Ye(叶一星), Yunyu Cai(蔡云雨), Jun Liu(刘俊), Shouliang Wu(吴守良), Pengfei Li(李鹏飞), Junhua Hu(胡俊华), Changhao Liang(梁长浩), and Yao Ma(马垚). Chin. Phys. B, 2022, 31(7): 078102.
[6] Structure, phase evolution and properties of Ta films deposited using hybrid high-power pulsed and DC magnetron co-sputtering
Min Huang(黄敏), Yan-Song Liu(刘艳松), Zhi-Bing He(何智兵), and Yong Yi(易勇). Chin. Phys. B, 2022, 31(6): 066101.
[7] Mg-doped layered oxide cathode for Na-ion batteries
Yuejun Ding(丁月君), Feixiang Ding(丁飞翔), Xiaohui Rong(容晓晖), Yaxiang Lu(陆雅翔), and Yong-Sheng Hu(胡勇胜). Chin. Phys. B, 2022, 31(6): 068201.
[8] Effect of Cu doping on the secondary electron yield of carbon films on Ag-plated aluminum alloy
Tiancun Hu(胡天存), Shukai Zhu(朱淑凯), Yanan Zhao(赵亚楠), Xuan Sun(孙璇), Jing Yang(杨晶), Yun He(何鋆), Xinbo Wang(王新波), Chunjiang Bai(白春江), He Bai(白鹤), Huan Wei(魏焕), Meng Cao(曹猛), Zhongqiang Hu(胡忠强), Ming Liu(刘明), and Wanzhao Cui(崔万照). Chin. Phys. B, 2022, 31(4): 047901.
[9] The 50 nm-thick yttrium iron garnet films with perpendicular magnetic anisotropy
Shuyao Chen(陈姝瑶), Yunfei Xie(谢云飞), Yucong Yang(杨玉聪), Dong Gao(高栋), Donghua Liu(刘冬华), Lin Qin(秦林), Wei Yan(严巍), Bi Tan(谭碧), Qiuli Chen(陈秋丽), Tao Gong(龚涛), En Li(李恩), Lei Bi(毕磊), Tao Liu(刘涛), and Longjiang Deng(邓龙江). Chin. Phys. B, 2022, 31(4): 048503.
[10] An n—n type heterojunction enabling highly efficientcarrier separation in inorganic solar cells
Gang Li(李刚), Yuqian Huang(黄玉茜), Rongfeng Tang(唐荣风), Bo Che(车波), Peng Xiao(肖鹏), Weitao Lian(连伟涛), Changfei Zhu(朱长飞), and Tao Chen(陈涛). Chin. Phys. B, 2022, 31(3): 038803.
[11] Anomalous strain effect in heteroepitaxial SrRuO3 films on (111) SrTiO3 substrates
Zhenzhen Wang(王珍珍), Weiheng Qi(戚炜恒), Jiachang Bi(毕佳畅), Xinyan Li(李欣岩), Yu Chen(陈雨), Fang Yang(杨芳), Yanwei Cao(曹彦伟), Lin Gu(谷林), Qinghua Zhang(张庆华), Huanhua Wang(王焕华), Jiandi Zhang(张坚地), Jiandong Guo(郭建东), and Xiaoran Liu(刘笑然). Chin. Phys. B, 2022, 31(12): 126801.
[12] Magnetohydrodynamic Kelvin-Helmholtz instability for finite-thickness fluid layers
Hong-Hao Dai(戴鸿昊), Miao-Hua Xu(徐妙华), Hong-Yu Guo(郭宏宇), Ying-Jun Li(李英骏), and Jie Zhang(张杰). Chin. Phys. B, 2022, 31(12): 120401.
[13] Molecular dynamics study of coupled layer thickness and strain rate effect on tensile behaviors of Ti/Ni multilayered nanowires
Meng-Jia Su(宿梦嘉), Qiong Deng(邓琼), Lan-Ting Liu(刘兰亭), Lian-Yang Chen(陈连阳), Meng-Long Su(宿梦龙), and Min-Rong An(安敏荣). Chin. Phys. B, 2021, 30(9): 096201.
[14] Probing thermal properties of vanadium dioxide thin films by time-domain thermoreflectance without metal film
Qing-Jian Lu(陆青鑑), Min Gao(高敏), Chang Lu(路畅), Fei Long(龙飞), Tai-Song Pan(潘泰松), and Yuan Lin(林媛). Chin. Phys. B, 2021, 30(9): 096801.
[15] Effect of Mo doping on phase change performance of Sb2Te3
Wan-Liang Liu(刘万良), Ying Chen(陈莹), Tao Li(李涛), Zhi-Tang Song(宋志棠), and Liang-Cai Wu(吴良才). Chin. Phys. B, 2021, 30(8): 086801.
No Suggested Reading articles found!