Please wait a minute...
Chin. Phys. B, 2011, Vol. 20(3): 037901    DOI: 10.1088/1674-1056/20/3/037901
CONDENSED MATTER: ELECTRONIC STRUCTURE, ELECTRICAL, MAGNETIC, AND OPTICAL PROPERTIES Prev   Next  

The charging stability of different silica glasses studied by measuring the secondary electron emission yield

Zhao Su-Ling(赵谡玲)a)† and Bertrand Poumellecb)‡
a Key Laboratory of Luminescence and Optical Information, Beijing Jiaotong University, Ministry of Education, Beijing 100044, China; b ICMMO/LPCES, UMR CNRS-UPS 8182, Université de Paris Sud, 91405 Orsay Cedex, France
Abstract  This paper reports that the charging properties of lead silica, Suprasil silica and Infrasil silica are investigated by measuring the secondary electron emission (SEE) yield. At a primary electron beam energy of 25 keV, the intrinsic SEE yields measured at very low injection dose are 0.54, 0.29 and 0.35, respectively for lead silica, Suprasil and Infrasil silica glass. During the first e-beam irradiation at a high injection current density, the SEE yields of lead silica and Suprasil increase continuously and slowly from their initial values to a steady state. At the steady state, the SEE yields of lead silica and Suprasil are 0.94 and 0.93, respectively. In Infrasil, several charging and discharging processes are observed during the experiment. This shows that Infrasil does not reach its steady state. Two hours later, all samples are irradiated again in the same place as the first irradiation at a low current density and low dose. The SEE yields of lead silica, Suprasil and Infrasil are 0.69, 0.76 and 0.55, respectively. Twenty hours later, the values are 0.62, 0.64 and 0.33, respectively, for lead silica, Suprasil and Infrasil. These results show that Infrasil has poor charging stability. Comparatively, the charging stability of lead silica is better, and Suprasil has the best characteristics.
Keywords:  secondary electron emission yield      charging stability      nonlinear silica glass  
Received:  08 December 2009      Revised:  15 October 2010      Accepted manuscript online: 
PACS:  79.20.Fr  
  77.22.Jp (Dielectric breakdown and space-charge effects)  
  42.65.Ky (Frequency conversion; harmonic generation, including higher-order harmonic generation)  

Cite this article: 

Zhao Su-Ling(赵谡玲) and Bertrand Poumellec The charging stability of different silica glasses studied by measuring the secondary electron emission yield 2011 Chin. Phys. B 20 037901

[1] Hsu W Y and Gupta M C 1992 Appl. Phys. Lett. 60 1
[2] Barbier D, Green M and Madden S J 1991 J. Lightwave Technol. 9 715
[3] Garcia Blanco S, Glidle A, Davies J H, Aitchison J S and Cooper J M 2001 Appl. Phys. Lett. 79 2889
[4] Syms R R A, Tate T J and Lewandowski J J 1994 J. Lightwave Technol. 12 2085
[5] Myers R A, Mukherjee N and Brueck S R J 1991 Opt. Lett. 16 1732
[6] Kazansky P G, Kamal A and Russell P St J 1993 Opt. Lett. 18 1141
[7] Kazansky P G, Kamal A and Russell P St J 1993 Opt. Lett. 18 693
[8] Qiu M, Pi F and Orriols G 1998 Appl. Phys. Lett. 73 3040
[9] Cheng G J, Xia Z F, Zhang Y W and Zhang H Y 1999 Acta Phys. Sin. 48 1676 (in Chinese)
[10] Cazaux J, Kim K H, Jbara O and Salace G 1991 J. Appl. Phys. 70 960
[11] Braga D, Poumellec B, Cannas V, Blaise G, Ren Y and Kristensen M 2004 J. Appl. Phys. 96 885
[12] Vallayer B, Blaise G and Treheux D 1999 Rev. Scientific Instrum. 70 3102
[13] Liebault J, Zarbout K, Moya G and Kallel A 2003 Journal of Non-Crystalline Solids 322 213
[14] Thome T, Braga D and Blaise G 2004 J. Appl. Phys. 95 2619
[15] Cazaux J 2004 J. Appl. Phys. 95 731
[16] Feldman C 1960 Phys. Rev. 117 455
[17] Murty R C 1965 Nature 207 398 endfootnotesize
[1] Analysis of secondary electron emission using the fractal method
Chun-Jiang Bai(白春江), Tian-Cun Hu(胡天存), Yun He(何鋆), Guang-Hui Miao(苗光辉), Rui Wang(王瑞), Na Zhang(张娜), and Wan-Zhao Cui(崔万照). Chin. Phys. B, 2021, 30(1): 017901.
No Suggested Reading articles found!