Abstract Secondary ion mass spectroscopy was used to study the chemical diffusivity of O18 in c-textured YBa2Cu3O7-$\delta$/SrTiO3 epitaxial thin film. By fitting experimental data to the one- dimensional diffusion curve, the apparent diffusivity along the c-axis was obtained to be equal to l.02×1014cm2/sec when the temperature was 350℃. A computer analysis method was put forward to calculate the "spiral diffusion" process, and the diffusivity anisotopy of films with different mosaic size obtained. For a film of 7000×7000?2 mosaic size, Dab was found to be ～3.55×10-5×exp((-1.03 ev)/kT) cm2/sec. The calculated results reveal that the variation of the results of Dc is not the result of diffusivity anisotropy but of the difference in mosaic size.
Received: 13 January 1998
Revised: 06 May 1998
Accepted manuscript online:
(Atomic, molecular, and ion beam impact and interactions with surfaces)
Cite this article:
CAI ZHEN (蔡震), JIN XUE-JUN (金学军) SIMS STUDY OF OXYGEN SPIRAL DIFFUSION C-TEXTURED Yba2Cu3O7-$\delta$/SrTiO3 EPITAXIAL THIN FILM 1998 Acta Physica Sinica (Overseas Edition) 7 912
Altmetric calculates a score based on the online attention an article receives. Each coloured thread in the circle represents a different type of online attention. The number in the centre is the Altmetric score. Social media and mainstream news media are the main sources that calculate the score. Reference managers such as Mendeley are also tracked but do not contribute to the score. Older articles often score higher because they have had more time to get noticed. To account for this, Altmetric has included the context data for other articles of a similar age.