Azobenzene mesogens mediated preparation of SnS nanocrystals encapsulated with in-situ N-doped carbon and their enhanced electrochemical performance for lithium ion batteries application

Meng Wang(王勐)1, Yang Zhou(周旸)1, Junfei Duan(段军飞)2, Dongzhong Chen(谌东中)1
1. Department of Polymer Science and Engineering, Key Laboratory of High Performance Polymer Materials and Technology of Ministry of Education, School of Chemistry and Chemical Engineering, Nanjing University, Nanjing 210023, China;
2. Department of Physics and Electronic Science, Changsha University of Science and Technology, Changsha 410076, China
Abstract  In this work, azobenzene mesogen-containing tin thiolates have been synthesized, which possess ordered lamellar structures persistent to higher temperature and serve as liquid crystalline precursors. Based on the preorganized tin thiolate precursors, SnS nanocrystals encapsulated with in-situ N-doped carbon layer have been achieved through a simple solventless pyrolysis process with the azobenzene mesogenic thiolate precursor served as Sn, S, N, and C sources simultaneously. Thus prepared nanocomposite materials as anode of lithium ion batteries present a large specific capacity of 604.6 mAh·g-1 at a current density of 100 mA·g-1, keeping a high capacity retention up to 96% after 80 cycles, and display high rate capability due to the synergistic effect of well-dispersed SnS nanocrystals and N-doped carbon layer. Such encouraging results shed a light on the controlled preparation of advanced nanocomposites based on liquid crystalline metallomesogen precursors and may boost their novel intriguing applications.
Keywords:  azobenzene-containing tin thiolates      liquid crystalline precursor      controlled synthesis      in-situ N-doped  
Received:  01 June 2016      Published:  05 September 2016
PACS:  61.30.-v (Liquid crystals)  
  81.07.Bc (Nanocrystalline materials)  
  82.47.Aa (Lithium-ion batteries)  
Fund: Project supported by the National Natural Science Foundation of China (Grant No. 21574062) and the Huaian High-Technology Research Institute of Nanjing University, China (Grant No. 2011Q1).
Corresponding Authors:  Junfei Duan, Dongzhong Chen     E-mail:;

Cite this article: 

Meng Wang(王勐), Yang Zhou(周旸), Junfei Duan(段军飞), Dongzhong Chen(谌东中) Azobenzene mesogens mediated preparation of SnS nanocrystals encapsulated with in-situ N-doped carbon and their enhanced electrochemical performance for lithium ion batteries application 2016 Chin. Phys. B 25 096102

[1] Donnio B 2014 Inorg. Chim. Acta 409 53
[2] Binnemans K 2009 J. Mater. Chem. 19 448
[3] Date R W, Iglesias E F, Rowe K E, Elliott J M and Bruce D W 2003 Dalton Trans. 10 1914
[4] Xiao X S, Lu W and Che C M 2014 Chem. Sci. 5 2482
[5] Kaur R and Mehta S K 2014 Coord. Chem. Rev. 262 37
[6] Ma H, Jiang L L, Li M, Li C X and Jiang Y R 2013 Chin. J. Liquid Cryst. Displ. 28 653
[7] Pang H, Zheng C W, Cao J H, Zhang X and Hua R M 2015 Chin. J. Liquid Cryst. Displ. 30 752
[8] Matioli E, Brinkley S, Kelchner K M, Hu Y L, Nakamura S, DenBaars S, Speck J and Weisbuch C 2012 Light Sci. Appl. 1 e22
[9] Wang L, Lin X W, Hu W, Shao G H, Chen P, Liang L J, Jin B B, Wu P H, Qian H, Lu Y N, Liang X, Zheng Z G and Lu Y Q 2015 Light Sci. Appl. 4 e253
[10] He Z H, Chen C P, Zhu J L, Yuan Y C, Li Y, Hu W, Li X, Li H J, Lu J G and Su Y K 2015 Chin. Phys. B 24 064203
[11] Wang Y, Shi J, Chen J, Zhu W and Baranoff E 2015 J. Mater. Chem. C 3 7993
[12] Su P Y S, Hsu S J, Tseng J C W, Hsu H F, Wang W J and Lin I J B 2016 Chem. Eur. J. 22 323
[13] Bisoyi H K and Kumar S 2011 Chem. Soc. Rev. 40 306
[14] Nealon G L, Greget R, Dominguez C, Nagy Z T, Guillon D, Gallani J L and Donnio B 2012 Beilstein J. Org. Chem. 8 349
[15] Duan J, Wang M, Bian H, Zhou Y, Ma J, Liu C and Chen D 2014 Mater. Chem. Phys. 148 1013
[16] Duan J, Ma J, Wu B, Li Q, Fang J and Chen D 2014 J. Mater. Chem. C 2 2375
[17] Cao X, Zheng B, Rui X, Shi W, Yan Q and Zhang H 2014 Angew. Chem. 126 1428
[18] Cao X, Yin Z and Zhang H 2014 Energy Environ. Sci. 7 1850
[19] Kim T K, Lee K J, Cheon J Y, Lee J H, Joo S H and Moon H R 2013 J. Am. Chem. Soc. 135 8940
[20] Yang S J, Nam S, Kim T, Im J H, Jung H, Kang J H, Wi S, Park B and Park C R 2013 J. Am. Chem. Soc. 135 7394
[21] Li Y, Tu J P, Huang X H, Wu H M and Yuan Y F 2007 Electrochem. Commun. 9 49
[22] Tao H C, Yang X L, Zhang L L and Ni S B 2014 J. Electroanal. Chem. 728 134
[23] Tripathi A M and Mitra S 2014 Rsc Adv. 4 10358
[24] Li S, Zheng J, Hu Z, Zuo S, Wu Z, Yan P and Pan F 2015 RSC Adv. 5 72857
[25] Hongtao L, Yan L, Zan W and Ping H 2010 Nanotechnology 21 105707
[26] Deng Z, Cao D, He J, Lin S, Lindsay S M and Liu Y 2012 ACS Nano 6 6197
[27] Biacchi A J, Vaughn D D and Schaak R E 2013 J. Am. Chem. Soc. 135 11634
[28] Zhu J, Wang D and Liu T 2013 Appl. Sur. Sci. 282 947
[29] Li S, Zuo S, Wu Z, Liu Y, Zhuo R, Feng J, Yan D, Wang J and Yan P 2014 Electrochim. Acta 136 355
[30] Peng H J, Hou T Z, Zhang Q, Huang J Q, Cheng X B, Guo M Q, Yuan Z, He L Y and Wei F 2014 Adv. Mater. Interfaces 1 1400227
[31] Qie L, Chen W M, Wang Z H, Shao Q G, Li X, Yuan L X, Hu X L, Zhang W X and Huang Y H 2012 Adv. Mater. 24 2047
[32] Kim C, Yang K S, Kojima M, Yoshida K, Kim Y J, Kim Y A and Endo M 2006 Adv. Func. Mater. 16 2393
[33] Zhu Z, Cheng F and Chen J 2013 J. Mater. Chem. A 1 9484
[34] Zhou X, Wan L J and Guo Y G 2013 Adv. Mater. 25 2152
[1] Controlled synthesis of ferromagnetic MnSex particles
Junjie Sun(孙俊杰), Chao Li(李超), Duo Chen(陈铎), Shishou Kang(康仕寿), Guolei Liu(刘国磊), Shuyun Yu(于淑云), Guangbing Han(韩广兵), Liangmo Mei(梅良模). Chin. Phys. B, 2016, 25(10): 107405.
[2] Morphology-controlled synthesis of SrTiO3 micro-scale particles
Cao Jia-Feng, Ji Yue-Xia. Chin. Phys. B, 2014, 23(12): 128104.
No Suggested Reading articles found!